MXLOC® PIPE SEALANT 13565
- Chemical Family
- Acrylics & Acrylates
MXLOC® PIPE SEALANT 13565 is designed for the sealing and locking of metal fittings and pipes. The product is a single component anaerobic, thixotropic, acrylic based product. The product cures when confined in the absence of air between close fitting metal surfaces and prevents leakage and loosening from vibration and shock.
Properties
- Physical Form
- Paste
Product families
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications
- Pipes & Plumbing
Product Families
- Anaerobic Adhesives
Other characteristics
- Brand
- MXLOC
- Features
Acid Resistant, Good Solvent Resistance, High Viscosity, Shock Absorbent, Solventless, Steam Resistant, Thixotropic, Vibration Damping
- Product Type
1K (1 component) Adhesive, Anaerobic Adhesive, Sealer; 1K (1 component) Adhesive; Anaerobic Adhesive; Sealer
- Compatible Substrates & Surfaces
- Metal
- Cure
- Anaerobic
- Markets
- Adhesives & Sealants
- Building & Construction
- Storage
Keep adhesive in a cool and dry place. The storage temperature is recommended at 8 °C to 24 °C. Shelf life is two years from the date of manufacture in the original container under the optimal conditions.
- Strength
- Low
- Viscosity
- High
- Appearance
- White to off - white paste
- Components
- One component – requires no mixing
- Shelf LIfe
- 24 months unopened when stored at 8 to 24 °C
- Technology
- Acrylic
- Ready-to-Use Products
- Precaution
1. Avoid contact with skin and eyes. 2. If contact with skin, rinse with water. 3. If adhesive gets into eye, keep eye open and rinse with water thoroughly. Seek medical attention immediately. 4. Keep the material out of children's reach.
- Chemical Type
- Methacrylate ester
- Secondary Cure
- Activator
- Labeling Claims
- Solvent-free
- Use Direction
For assembly 1. The substrate surfaces must be clean and free of grease. 2. Shake the product thoroughly before use. 3. If the cure speed is too slow, consider using activator. 4. Apply several drops to the nut & bolt. 5. Assemble and tighten as required. 6. To prevent the clogging of the bottle nozzle, do not let the tip touch the metal surfaces during application. For disassembly & cleanup 1. Use localized heat (250 ℃) to nut and bolt, disassemble while hot. 2. Use a wire brush to clean the charred product.
- General Information
This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be use with chlorine or other strong oxidizing materials. Where washing systems are used to clean the surfaces before bonding, it is important to check the compatibility of the washing solution with the adhesive. In some cases, these solutions can affect the cure and performance of the adhesive. This product is not recommended for use on certain plastics. Users are recommended to confirm compatibility of the product with such substrates.
- Certifications and Compliance
- NSF Approved
- Chemical Resistance
Aged under conditions indicated and tested @ 25 ℃
- Ready to Use Product Features
- Acid Resistant
- Good Solvent Resistance
- High Viscosity
- Shock Absorbent
- Solventless
- Steam Resistant
- Thixotropic
- Vibration Damping
- Compatible Substrates and Surfaces
- Metal
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity (25°C) | 1.1 | g/cm³ |
| Viscosity, Brookfield - RVT (25°C) (Spindle 3, 2.5 rpm) | 175,000 to 525,000 | mPa·s (cP) |
Table 2 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Breakaway Torque (M10 steel nuts and bolts) (Cured for 24 hrs at 25 °C) | 25.0 | lb.in | ISO 10964 |
| Breakaway Torque (M10 Zinc dichromate nuts and bolts) (Cured for 24 hrs at 25 °C) | 22.0 | lb.in | ISO 10964 |
| Prevail Torque (180°) (M10 steel nuts and bolts) | 8.0 | lb.in | ISO 10964 |
| Prevail Torque (180°) (M10 Zinc dichromate nuts and bolts) | 5.0 | lb.in | ISO 10964 |
| Breakloose Torque (Pre-torque to 5 N․m) (M10 steel nuts and bolts) | 68.0 | lb.in | ISO 10964 |
| Breakloose Torque (Pre-torque to 5 N․m) (M10 Zinc dichromate nuts and bolts ) | 52.0 | lb.in | ISO 10964 |
| Prevail Torque at 180° (Pre-torque to 5 N․m) (M10 steel nuts and bolts) | 6.0 | lb.in | ISO 10964 |
| Prevail Torque at 180° (Pre-torque to 5 N․m) (M10 Zinc dichromate nuts and bolts) | 6.0 | lb.in | ISO 10964 |
| Compressive Shear Strength (Steel pins and collars) (After 30 minutes at 25 °C) | 174.0 | psi | ISO 10123 |
| Compressive Shear Strength (Steel pins and collars) (After 24 hours at 25 °C) | 232.0 | psi | ISO 10123 |