MXBON® GENERAL PURPOSE 22460
MXBON® GENERAL PURPOSE 22460 is a low blooming and low odor cyanoacrylate adhesive, and it is specially formulated for the assembly of a variety of plastic, metal and rubbers. It is specially formulated for the assembly of difficult-to-bond materials. It will highly polymerize with moisture in the air for a fast cure and meet the highest industrial standards.
Properties
- Physical Form
- Liquid
Product families
- Contact Adhesives
Other characteristics
- Brand
- MXBON
- Cure Method
- Moisture Cure
- Product Type
- 1K (1 component) Adhesive, Contact Adhesive
- 1K (1 component) Adhesive
- Contact Adhesive
- Compatible Substrates & Surfaces
Aluminum, Elastomers & Rubbers, Leather, Metal, Plastics, Steel, Wood
- Base
- 2 - Methoxyethyl 2 - Cyanoacrylate
- Cure
- Moisture
- Moisture Cure
- Color
- Transparent
- Markets
- Adhesives & Sealants
- Industrial
- Storage
Keep in a cool area out of direct sunlight. Refrigeration to 5°C gives optimum storage stability. When stored in a refrigerator, allow the adhesive to gradually warm to room temperature prior to use. It will prevent condensation inside the bottle which can reduce shelf life
- Appearance
Transparent, colorless to yellowish colored liquid
- Components
- Single part – requires no mixing or heating
- Shelf LIfe
- 18 months unopened when stored at 5 - 10 °C
- Technology
- Ready-to-Use Products
- Labeling Claims
- Solvent-free
Technical data
Table 1 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Side Impact Strength (Aluminum) (Cured for 72 hrs at 25°C) | 1.4 - 2.4 | ft-lb/in2 | ASTM D950 |
| Coefficient of Thermal Expansion | 90 × 10^- 6 | mm/mm/K | ISO 11359-2 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (25°C) | 1.1 | g/cm³ | — |
| Viscosity, Brookfield (25 °C) | 25 - 55 | mPa. s (cP) | ISO 3104/3105 |
| Service Temperature Range | - 54~100 ( - 65~212) | °C (°F) | — |
| Full Cure | 24.0 | hrs | — |
Table 3 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Conductivity | 0.1 | W/mK | ISO 8302 |
| Glass Transition Temperature | 120.0 | °C | ISO 11359-2 |
| Hardness | 78.0 | Shore D | ISO 868 |
| Dielectric Constant (10kHz) | 2.5 | — | IEC 60250 |
| Dielectric Breakdown Strength | 25.0 | kV/mm | IEC 60243-1 |
| Surface Resistivity | 5 - 9 × 10^15 | Ω | — |
| Volume Resistivity | 5 - 9 × 10^15 | Ωcm | IEC 60093 |
| Dielectric Dissipation Factor (10kHz) | max. 0.025 | — | IEC 60250 |
Table 4 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Lap Shear Strength GBMS (Grit Blasted Mild Steel) (Cured for 72 hrs at 25 °C) | 3221.6 | psi | ISO 4587/ASTM D1002/JIS K6850 |
| Aluminum A5754 (Cured for 72 hrs at 25 °C) | 1125.1 | psi | ISO 4587/ASTM D1002/JIS K6851 |
| ABS (Grit Blasted Mild Steel) (Cured for 72 hrs at 25 °C) | 1274.4 | psi | ISO 4587/ASTM D1002/JIS K6852 |
| PVC (Polyvinyl chloride) (Cured for 72 hrs at 25 °C) | 1236.0 | psi | ISO 4587/ASTM D1002/JIS K6853 |
| PC (Polycarbonate) (Cured for 72 hrs at 25 °C) | 1402.4 | psi | ISO 4587/ASTM D1002/JIS K6854 |
| NBR (Nitrile-Butadiene Rubber) (Cured for 72 hrs at 25 °C) | 101.0 | psi | ISO 4587/ASTM D1002/JIS K6850 |
| Block Tensile Strength (Stainless Steel) (Cured for 72 hrs at 25 °C) | 4649.6 | psi | ISO 6922/ASTM D2095/JIS K6849 |
| Side Impact Strength (Stainless Steel) (Cured for 72 hrs at 25°C) | 1.4 - 2.4 | ft-lb/in2 | ASTM D950 |