Neviprop 043 FV25 NERO
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Neviprop 043 FV25 NERO is a Polypropylene reinforced with 25% glass fiber. its used in Automotive & Agricolture Consumer Goods
Product families
Applications
Applications
- Consumer Goods — Other Consumer Goods Applications
Agriculture & Feed — Agricultural Films
- Greenhouse & Tunnel Films
- Mulch & Fumigation Films
- Other Agricultural Films
- Silage & Stretch Films
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Other Automotive Applications
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Neviprop
- Polymer Name
- Polypropylene (unspecified)
- Fillers Included
- Glass Fiber
- Markets
- Agriculture & Feed
- Automotive & Transportation
- Consumer Goods
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Chemical Resistant
- Excellent Mechanical Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Agricultural Applications
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Consumer Applications
- Greenhouse Film
- Mulch Film
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Break at 23°C | 65 | MPa | ISO 527-1/2 |
| Tensile Stress at Break (23°C, 5mm/min) | 65 | MPa | ISO 527-1/2 |
| Tensile Strain at Break at 23°C | 4 | % | ISO 527-1/2 |
| Tensile Strain at Break (23°C, 5mm/min) | 4 | % | ISO 527-1/2 |
| Tensile Elastic modulus 23°C (1 mm/min) | 6000 | MPa | ISO 527-1/2 |
| Tensile Elastic Modulus (23°C, 1mm/min) | 6000 | MPa | ISO 527-1/2 |
| Flexural Maximum Load at 23°C (2 Mm/Min) | 100 | MPa | ISO 178 |
| Flexural Modulus at 23°C | 4500 | MPa | ISO 178 |
| Flexural Modulus (23°C, 2mm/min) | 4500 | MPa | ISO 178 |
| Izod Impact Strength Notched at 23°C (80 x 10 x 4.0 mm) | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact Strength Notched (23°C, 80 x 10 x 4.0 mm) | 7 | kJ/m2 | ISO 180/1A |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| VICAT Softening Point (50 N - 50°C/h) | 130 | °C | ISO 306/B |
| VICAT Softening Point (50N, 50°C/h) | 130 | °C | ISO 306/B |
| Heat Deflection Temperature (1,80 MPa - 120°C/h) | 145 | °C | ISO 75-1/-2 |
| Heat Deflection Temperature (1.80 MPa, 120°C/h) | 145 | °C | ISO 75-1/-2 |
Table 3 of 4
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density at 23°C | 1,09 | g/cm3 | ISO 1183 |
| Density (23°C) | 1.09 | g/cm3 | ISO 1183 |
| Melt Volume Flow Rate - MVR at 190°C-2,16kg | 6 | cm3/10min | ISO 1133 |
| Melt Flow Index (190°C, 2.16 kg) | 6 | cm3/10min | ISO 1133 |
| Shrinkage - Parallel (115mm x 50mm x 3mm) | 0,2 - 0,5 | % | Internal |
| Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.2 - 0.5 | % | Internal |
| Shrinkage - Normal (115mm x 50mm x 3mm) | 0,4 - 0,8 | % | Internal |
| Shrinkage - Normal (115mm x 50mm x 3mm) | 0.4 - 0.8 | % | Internal |
| Melt Temperature | 210 - 250 | °C | — |
| Mould Temperature | 50 - 70 | °C | — |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Burning Behaviour | HB | UL94 |