Nevies 029 FV17 NATURALE
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
Nevies 029 FV17 NATURALE is a ABS reinforced with 17% glass fiber. its used in Consumer Goods
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Nevies
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Glass Fiber
- Markets
- Consumer Goods
- Applications
Consumer Goods — Other Consumer Goods Applications
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Good Aesthetics
- Low Warpage
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Consumer Applications
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Break at 23°C | 75 | MPa | ISO 527-1/2 |
| Tensile Stress at Break (23°C) | 75 | MPa | ISO 527-1/2 |
| Tensile Strain at Break at 23°C | 3 | % | ISO 527-1/2 |
| Tensile Strain at Break (23°C) | 3 | % | ISO 527-1/2 |
| Tensile Elastic modulus 23°C (1 mm/min) | 6300 | MPa | ISO 527-1/2 |
| Tensile Elastic Modulus (23°C, 1mm/min) | 6300 | MPa | ISO 527-1/2 |
| Izod Impact Strength Unnotched at 23°C | 13 | kJ/m2 | ISO 180/1U |
| Izod Impact Strength Unnotched (23°C) | 13 | kJ/m2 | ISO 180/1U |
| Izod Impact Strength Notched at 23°C | 6.5 | kJ/m2 | ISO 180/1A |
| Izod Impact Strength Notched (23°C) | 6.5 | kJ/m2 | ISO 180/1A |
Table 2 of 3
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density at 23°C | 1.16 | g/cm3 | ISO 1183 |
| Density (23°C) | 1.16 | g/cm3 | ISO 1183 |
| Melt Volume Flow Rate - MVR at 220°C, 10 kg) | 10 | cm3/10min | ISO 1183 |
| Melt Volume Flow Rate (220°C, 10 kg) | 10 | cm3/10min | ISO 1183 |
| Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.1 – 0.3 | % | Internal |
| Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.1 - 0.3 | % | Internal |
| Shrinkage - Normal (115mm x 50mm x 3mm) | 0.3 – 0.6 | % | Internal |
| Shrinkage - Normal (115mm x 50mm x 3mm) | 0.3 - 0.6 | % | Internal |
| Drying Temperature | 80 | °C | — |
| Drying Time | 4 | h | — |
| Burning behaviour (3.2 mm) | HB | — | sec. - acc.to UL94 |
| Melt Temperature | 230 - 260 | °C | — |
Table 3 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| VICAT Softening Point (50 N, 50°C/h) | 100 | °C | ISO 306/B |
| VICAT Softening Point (50N, 50°C/h) | 100 | °C | ISO 306/B |
| Heat Deflection Temperature (1,80 MPa - 120°C/h) | 95 | °C | ISO 75-1/-2 |
| Heat Deflection Temperature (1.80 MPa, 120°C/h) | 95 | °C | ISO 75-1/-2 |