Neviester B1 V30 NATURALE
- Chemical Family
- Polyesters
Neviester B1 V30 NATURALE is a natural color. Its used in Electric & Electronic Consumer Goods.
Product families
Applications
Applications
- Consumer Goods — Other Consumer Goods Applications
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Neviester
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Chemical Resistant
- Excellent Mechanical Strength
- Low Warpage
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Consumer Applications
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Break at 23°C | 120 | MPa | ISO 527-1/2 |
| Tensile Stress at Break (23°C, 5mm/min) | 120 | MPa | ISO 527-1/2 |
| Tensile Strain at Break at 23°C | 3 | % | ISO 527-1/2 |
| Tensile Strain at Break (23°C, 5mm/min) | 3 | % | ISO 527-1/2 |
| Tensile Elastic modulus 23°C (1 mm/min) | 9000 | MPa | ISO 527-1/2 |
| Tensile Elastic Modulus (23°C, 1mm/min) | 9000 | MPa | ISO 527-1/2 |
| Izod Impact Strength Unnotched at 23°C | 50 | kJ/m2 | ISO 180/1U |
| Izod Impact Strength Unnotched (23°C) | 50 | kJ/m2 | ISO 180/1U |
| Izod Impact Strength Notched at 23°C | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact Strength Notched (23°C) | 7 | kJ/m2 | ISO 180/1A |
Table 2 of 4
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density at 23°C | 1.53 | g/cm3 | ISO 1183 |
| Density (23°C) | 1.53 | g/cm3 | ISO 1183 |
| Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.2 – 0.4 | % | Internal |
| Shrinkage - Parallel (115mm x 50mm x 3mm) | 0.2 - 0.4 | % | Internal |
| Shrinkage - Normal (115mm x 50mm x 3mm) | 0.8 – 1.2 | % | Internal |
| Shrinkage - Normal (115mm x 50mm x 3mm) | 0.8 - 1.2 | % | Internal |
| Drying Temperature | 120 | °C | — |
| Drying Time | 4 | h | — |
| Melt Temperature | 240 - 280 | °C | — |
| Mould Temperature | 80 – 120 | °C | — |
| Mould Temperature | 80 - 120 | °C | — |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| VICAT Softening Point (50 N, 50°C/h) | 205 | °C | ISO 306/B |
| VICAT Softening Point (50N, 50°C/h) | 205 | °C | ISO 306/B |
| Heat Deflection Temperature (1,80 MPa - 120°C/h) | 200 | °C | ISO 75-1/-2 |
| Heat Deflection Temperature (1.80 MPa, 120°C/h) | 200 | °C | ISO 75-1/-2 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Burning Behaviour | HB | UL94 |