QuakeBond™ 220UR
- Chemical Family
- Epoxy & Epoxy Derivatives
QuakeBond™ 220UR is a two-component high-strength structural epoxy adhesive designed for a variety of applications including underwater marine uses. This adhesive system trowels easily and has an immediate high tack consistency both in ambient and underwater construction. QuakeBond™ 220UR is a 100% solids formulation with low toxicity, low odor during the cure.
Other characteristics
- Brand
- QuakeBond
- Product Type
2K (2 component) Adhesive, Epoxy Adhesive, Solvent free (100% Solids) Adhesive; 2K (2 component) Adhesive; Epoxy Adhesive; Solvent free (100% Solids) Adhesive
- Application Method
- Trowel
- Compatible Substrates & Surfaces
- Concrete, Masonry, Metal, Steel, Stone, Wood
- Usage
Adhesive for bonding external reinforcement to concrete, masonry, wood, stone, steel, etc.; Structural bonding of QuakeWrap®, PipeMedic®, PileMedic® SpiRe products.; Structural bonding of saturated fabrics on vertical and overhead surfaces.; Interlayer surface coating for multiple-ply installations.
- Cleanup
Collect with absorbent material, flush with water.; Clean up using acetone or other ketone solvents.; Dispose waste in accordance with local disposal regulations.
- Markets
- Automotive & Transportation
- Building & Construction
- PACKAGING
- 3gallon (11.4 L) kits.
- 15gallon (56.8 L) kits.
- 30.4 oz. (900 mL) cartridges.
- Advantages
High strength structural paste adhesive.; Non-sag consistency is ideal for vertical and overhead applications.; Fully compatible with QuakeWrap® laminate and saturated fabric systems.; Paste consistency is ideal for underwater applications.; Convenient 2:1 mix ratio, by weight or volume.; 100% solvent-free.; Moisture tolerant.; 12-hour full cure.; Non-toxic when fully cured.; Product DOT non-corrosive for shipping.
- Application
Air and surface temperature should be between 45 - 95 °F (7 - 35 °C).; Do not begin application if air, substrate, or material temperatures is below 45°F (7°C) or expected to fall below 45°F (7°C) within 12 hours of application.; Do not begin application if the dew point is within 5°F (3°C) of the temperature.; Variations in temperature can affect the pot life and sag properties of this material.; Apply product to substrate with a putty knife or trowel and smooth to appropriate thickness.
- Limitations
QuakeBond™ 220UR will not cure in temperatures below 40°F.; Seek approval from a QuakeWrap representative for applications of the product below 45°F.; All epoxies will show chalking/yellowing on exterior exposures.; Application of epoxy coatings in cool temperatures and high humidity can result in the formation of amine blush.; Blush may appear as a milky, white, tacky residue on the surface of the cured coating and must be removed before the application of another coat.; Intercoat adhesion problems may occur if blush is not removed.
- Technology
- Ready-to-Use Products
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity (Mixed) | Non-Sag Paste | — | — |
| Mix Ratio (Weight, A:B) | 2:1 | — | — |
| Pot Life (77°F) | 30.0 | minutes | — |
| Full Cure Time | 12.0 | hours | — |
| Tensile Strength | 5598.0 | psi | ASTM D-638 |
| Compressive Strength | 13200.0 | psi | ASTM D-695 |
| Shear Strength | 2400.0 | psi | ASTM D-1002 |
| Flexural Strength | 9000.0 | psi | ASTM D-790 |
| Adhesion to Concrete | Substrate Failure | — | — |
| Adhesion to Steel | min. 1,200 | psi | SSPC-SP10 |
| Adhesion to Damp Concrete (Substrate Failure) | min. 350 | psi | — |
| Tensile Elongation | 3.0 | % | — |