QuakeBond™ 220-TC
- Chemical Family
- Epoxy & Epoxy Derivatives
QuakeBond™ 220-TC (Tack coat) is a two-component high-strength structural epoxy resin designed for structural adhesion. This adhesive system trowels easily and has high tackiness. QuakeBond™ 220-TC is a 100% solids formulation with low toxicity, low odor during cure, and features a unique pot life of 130-minutes for longer workability.
Product families
Applications
- Construction Adhesives
Product Families
- Structural Adhesives
Other characteristics
- Brand
- QuakeBond
- Product Type
2K (2 component) Adhesive, Epoxy Adhesive, Solvent free (100% Solids) Adhesive; 2K (2 component) Adhesive; Epoxy Adhesive; Solvent free (100% Solids) Adhesive
- Application Method
- Trowel
- Compatible Substrates & Surfaces
- Concrete, Masonry, Metal, Steel, Stone, Wood
- Usage
Adhesive for bonding external reinforcement to concrete, masonry, wood, stone, steel, etc.; Structural bonding of QuakeWrap®, PipeMedic®, PileMedic® and SpiRe products.; Structural bonding on vertical and overhead surfaces.
- Cleanup
Collect with absorbent material, clean up using acetone or other ketone solvents.
- Markets
- Building & Construction
- PACKAGING
- 3-gallon (11.4 L) kits.
- 15-gallon (56.8 L) kits.
- Advantages
- High strength, structural paste adhesive.
- High tackiness for overhead applications.
- 100% solvent-free.
- Moisture tolerant.
- 24-hour cure time.
- Non-toxic when fully cured.
- Product DOT non-corrosive for shipping.
- Application
Air and surface temperature should be between 45-95°F (7-35°C).; Do not begin application if air, substrate, or material temperatures is below 45°F (7°C) or expected to fall below 45°F (7°C) within 24 hours of application.; Do not begin application if the dew point is within 5°F (3°C) of the temperature.; Temperature variations can affect the pot life and sag properties of this material.; Apply product to substrate with a putty knife or trowel and smooth to appropriate thickness.
- Limitations
QuakeBond™ 220TC will not cure in temperatures below 40°F.; Seek approval from a QuakeWrap representative for applications of the product below 45°F.; All epoxies will show chalking/yellowing on exterior exposures.; Application of epoxy coatings in cool temperatures and high humidity can result in the formation of amine blush.; Blush may appear as a milky, white, tacky residue on the surface of the cured coating and must be removed before the application of another coat.; Intercoat adhesion problems may occur if blush is not removed.
- Technology
- Ready-to-Use Products
- Labeling Claims
- Non-Corrosive
- Application Methods
- Trowel
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity (Mixed) | Non-Sag Paste | — | — |
| Mix Ratio (Weight, A:B) | 100:42.5 | — | — |
| Pot Life (77°F) | 137.0 | minutes | — |
| Full Cure Time | 24.0 | hours | — |
| Tensile Strength | 4360.0 | psi | ASTM D-638 |
| Shear Strength | 2300.0 | psi | ASTM D-1002 |
| Flexural Strength | 9000.0 | psi | ASTM D-790 |
| Adhesion to Concrete | Substrate Failure | — | — |
| Adhesion to Steel | min. 1,200 | psi | SSPC-SP10 |
| Adhesion to Damp Concrete (Substrate Failure) | min. 350 | psi | — |
| Tensile Elongation | 3.0 | % | — |
| Hardness | 85 - 90 | Shore D | — |