ROSECO® CSB X2
- Chemical Family
- Modifed StarchesStarches
ROSECO® CSB X2 is a bio-compostable starch compound resin derived from tapioca starch and biopolymers, excels in delivering high bio-content and exceptional mechanical properties. Designed for blown film applications, this warm beige pellet resin offers superior translucence and mechanical performance. With a significant renewable material content, CSB X2 effectively reduces the carbon footprint in end products while enhancing functionality and mechanical attributes. It's also easily processed using conventional extrusion machinery.
Properties
- Physical Form
- Microgranule
- Pellets
- Solid
Product families
- Biodegradable Polymers
Other characteristics
- Brand
- ROSECO
- Density
- 1,200.0 - 1,400.0 kg/m³
- Polymer Name
- Thermoplastic Starch (TPS)
- Labeling Claims
Bio-based, Biodegradable, Low Carbon Footprint (PCF); Bio-based; Biodegradable; Low Carbon Footprint (PCF)
- Processing Methods
- Blown Film Extrusion, Extrusion, Film Extrusion
- Appearance
- Warm beige pellet
- Processing
This material can be used without drying. In case of broken packaging, it is recommended to be dried at 60°C for 4 hours prior to the processing.
- Shelf LIfe
- 12 Months
- Technology
- Plastics
- Packaging Type
- Bags
- Color
- Beige
- Material Features
- Compostable
- Good Mechanical Properties
- Good Processability
- Renewable Resource Content
- Translucent
- Storage Condition
Well-sealed package should be stored under cool and dry place out of direct sunlight.
- Benefits and Features
Roseco CSB X2 offers high translucent and mechanical performances for blown film applications. With high content of renewable materials, Roseco CSB X2 can reduces carbon footprint in final products with a functional and mechanical improvement; meanwhile, processable on conventional extrusion machinery.
- Packaging Information
This product is packed in sealed-moisture proof 25 kg bag.
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Extrusion
- Film Extrusion
Technical data
Table 1 of 2
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Content | max. 1 | % | ASTM D6980 |
| Density | 1.20 - 1.40 | g/cm³ | ASTM D792 |
| Melt Flow Index (190°C, 2.16 kg) | 2 - 6 | g/10 min | ASTM D1238 |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Modulus (MD) | min. 50 | MPa | ASTM D882 |
| Modulus (TD) | min. 55 | MPa | ASTM D882 |
| Tensile Strength (MD) | min. 27 | MPa | ASTM D882 |
| Tensile Strength (TD) | min. 22 | MPa | ASTM D882 |
| Elongation (at break, MD) | min. 410 | % | ASTM D882 |
| Elongation (at break, TD) | min. 680 | % | ASTM D882 |