Nexa3D xPP405-Black
Nexa3D xPP405-Black is a high elongation and high toughness material with outstanding impact resistance and excellent surface finish.This stiff and durable high performance material is ideal for a wide variety of tools in the production floor, including manufacturing aids and final parts such as housings and consumer goods applications. The unique set of perform anceattributes makes it comparable to an unfilled thermoplastic like polypropylene. Parts can be printed with various DLP printersand machined, tapped, or polished for final finish.
Product families
Applications
- Tooling & Moldmaking
Product Families
- Photoactive Resins
Other characteristics
- Density
- 1046.0 - 1046.0 kg/m³
- End Uses
Consumer Applications, Housings, Molds/Dies/Tools, Power/Other Tools
- Tensile Strength
- 23.0 - 25.0 MPa
- Processing Methods
- 3D Printing, Digital Light Processing
- Color
- Black
- Markets
- Industrial
- Limitations
Vat Printer : xPP405-Black formula is not possible. Post Cure : xPP405-Black requires UV/Visible light post curing.
- Post Curing
xPP405-Black requires post curing to achieve specified properties. A wide array of post cure equipment can be used to cure xPP405-Black appropriately.
- Technology
- Plastics
- Post Processing
xPP405-Black requires post processing to achieve specified properties. Prior to post curing, support structures should be removed from the printed part, and the part should be washed in a compatible cleaner. Nexa3D recommends either IPA or Cleaner C in 2 minute interval wash cycles. Use compressed air to remove residual solvent from the surface of the material between intervals.
- Material Features
- Durable
- Excellent Toughness
- Excellent UV Stability
- Good Machinability
- Good Stiffness
- Good Surface Finish
- Good Weather Stability
- High Elongation
- Chemical Inventories
- DSL (Canada)
- NDSL (Canada)
- TSCA (USA)
- TSCA Exempt (USA)
- Certifications and Compliance
- California Proposition 65
- Additional Development Options
- Colors
- xPP405-Black formula can be made in additional pigment colors. LCD
- Printers
- xPP405-Black currently testing, there's potential.
- Plastics and Elastomers End Uses
- Consumer Applications
- Housings
- Molds/Dies/Tools
- Power/Other Tools
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- 3D Printing
- Digital Light Processing
Technical data
Table 1 of 1
21 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Break (Green)²¹ | 23 - 25 | MPa | ASTM D638 |
| Tensile Stress at Yield (Green)²¹ | 24 - 26 | MPa | ASTM D638 |
| Young’s Modulus (Green)²¹ | 877 - 917 | MPa | ASTM D638 |
| Elongation at Failure (Green)²¹ | 81 - 97 | % | ASTM D638 |
| Tensile Stress at Break (Post Processed)¹⁷ | 33 - 37 | MPa | ASTM D638 |
| Tensile Stress at Yield (Post Processed)¹⁷ | 37 - 39 | MPa | ASTM D638 |
| Young’s Modulus (Post Processed)¹⁷ | 1267 - 1333 | MPa | ASTM D638 |
| Elongation at Failure (Post Processed)¹⁷ | 88 - 112 | % | ASTM D638 |
| Maximum Flexural Stress(Post Processed)²⁰ | 44 - 46 | MPa | ASTM D790 |
| Flexural Modulus (Post Processed)²⁰ | 1235 - 1365 | MPa | ASTM D790 |
| Flexural Strain at Break (Post Processed)²⁰ | Does not break | — | ASTM D790 |
| Impact Strength - IZOD Notched (Post Processed)¹⁸ | 60 - 64 | J/m | ASTM D256 |