Nexa3D 3843-xABS Black
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)
Nexa3D 3843-xABS Black is a high performance, high modulus product which boasts excellent flexural and tensile physical properties with a relatively high degree of elongation. Nexa3D 3843-xABS Black displays high green strength and good Heat DeflectionTemperature enabling it to print accurately and function in a wide variety of applications. Nexa3D3843-xABS Black has been tested in QUV exterior weathering conditions (ASTM G-154) for 800 hours with less than a 15% change in Tensile and IZOD Impact properties.
Product families
Applications
- Equipment & Parts
- Tooling & Moldmaking
Product Families
- Photoactive Resins
Other characteristics
- Density
- 1100.0 - 1100.0 kg/m³
- End Uses
- Fixtures, Jigs, Modeling Material, Prototyping
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Tensile Strength
- 31.0 - 33.0 MPa
- Processing Methods
- 3D Printing
- Color
- Black
- Markets
- Industrial
- Appearance
- Black
- Technology
- Plastics
- Use Direction
This product is light sensitive; exposure to daylight, UV light and artificial lighting should be kept to a minimum during storage and handling.; Shake or stir Nexa3D 3843-xABS Black well before use.; Agitate resin before each print; Do not leave resin in printer tray when not in use
- Material Features
- Durable
- Excellent Flexural Modulus
- Excellent Tensile Properties
- Good Aesthetics
- Good Green Strength
- Good Stiffness
- Good Toughness
- Good Weather Stability
- Storage Information
Store product in the unopened container in a dry location.; Storage information may be indicated on the product container labeling.; Optimal Storage : 8°C to 21°C.; Storage below 8°C or greater than 28°C can adversely affect product properties.; Material removed from containers may be contaminated during use. Do not return product to the original container. Nexa3D cannot assume responsibility for product which has been ontaminated or stored under conditions other than those previously indicated.
- Chemical Inventories
- DSL (Canada)
- NDSL (Canada)
- TSCA (USA)
- Certifications and Compliance
- California Proposition 65
- 3D Printing Machine Settings
Cure rate and ultimate depth of cure depend on light intensity, spectral distribution of the light source, exposure time and light transmittance of the printer window through which the light must pass.. The following working curve values were determined using a NXE400 printer.
- Plastics and Elastomers End Uses
- Fixtures
- Jigs
- Modeling Material
- Prototyping
- Plastics and Elastomers Functions
- Resin
- Recommended Post Print Processing
Rinse the printed part using an approved cleaner to remove uncured resin; The use compressed air or impregnated wipes to remove excess residual solvent from the surface is recommended; Remove any support structures prior to any post-curing step
- Plastics and Elastomers Processing Methods
- 3D Printing
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Break | 31 - 33 | MPa | ASTM D638 |
| Young’s Modulus | 1348 - 1452 | MPa | ASTM D638 |
| Elongation at Failure | 42 - 58 | % | ASTM D638 |
| Flexural Stress at Yield | 28.7 - 31.3 | MPa | ASTM D790 |
| Flexural Modulus | 1270 - 1530 | MPa | ASTM D790 |
| Flexural Strain at Break | min. 10 | % | ASTM D790 |
| IZOD Impact strength (Notched) | 50.8 - 56.8 | J/m | ASTM D256 |
| HDT (at 0.455 MPa, Vicat) | 56 | °C | ASTM D648 |
| Water Absorption | 2.35 | % | ASTM D570 |
Table 2 of 2
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity (25°C) | 1.1 | g/cm³ |
| Viscosity (25°C) | 450 - 750 | mPa*s |