Nils Malmgren AB NM Resin 094
- Chemical Family
- Epoxy & Epoxy Derivatives
NM Resin 094 together with NM Hardener 093 C is a low viscosity epoxy resin for manufacturing of sand molds and laminates. The resin can be accelerated with up to 10% of NM Accelerator 254. At increased amounts of accelerator, potlife and exotermic are affected. When having large molds, the accelerator should not be added.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Tooling & Moldmaking
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- End Uses
- Mold Making
- Polymer Name
- Epoxy Resins & Compounds
- Markets
- Industrial
- Pot Life
Potlife for NM Resin 094 / NM Hardener 093 C with different amounts of NM Accelerator 254. The values are for 100 gms of NM Resin 094 / NM Hardener 093 C with a initial temperature of 20°C. The percent adding is calculated as ex. 100 gms + 1 gm.
- Technology
- Composite Materials
- Normal Packing
- 13.0 + 4.8 = 17.8 kg
- Chemical Resistance
- Acetone
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Plastics and Elastomers End Uses
- Mold Making
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Resin | NM Gjutharts 094 | — |
| Hardener | NM Härdare 093 C | — |
| Accelerator | NM Accelerator 254 | — |
| Mixing Ratio (Weight, Volume) | 100 - 37 (100 - 44) | — |
| Density (Resin) | 1159 | kg/m3 |
| Density (Hardener) | 965 | kg/m3 |
| Density (Accelerator) | 1146 | kg/m³ |
| Viscosity (25°C Resin) | 3500 | mPa·s |
| Viscosity (25°C Hardener) | 22 | mPa·s |
| Viscosity (25°C Accelerator) | 65 | mPa·s |
| Mixture | 500 | mPa·s |
| Tensile Strength (0% 254, 6% 254) | 52 (55 ) | MPa |