Nils Malmgren AB NM Laminating 380 A
- Chemical Family
- Epoxy & Epoxy Derivatives
NM Laminating 380 A is a very low viscosity epoxy resin specially designed for good wetting and adhesion to glass-carbon-polyester- and aramide fibers. NM Laminating 380 A shall gel at room temperature or just above. Full cure at 60°C, 24 hours.The low viscosity makes NM Laminating 380 A suitable for injection.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Tooling & Moldmaking
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- End Uses
- Mold Making
- Polymer Name
- Epoxy Resins & Compounds
- Color
- Transparent
- Markets
- Industrial
- Technology
- Composite Materials
- Chemical Resistance
- Acetone
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Plastics and Elastomers End Uses
- Mold Making
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit |
|---|---|---|
| Cleaning Solvent | Acetone | — |
| Resin | NM Laminering 380 A | — |
| Hardener | NM Härdare 380 B | — |
| Mixing Ratio (Weight, Volume) | 100 - 35 (100 - 41.68) | — |
| Density | 1100 | kg/m3 |
| Density 380 A, 20°C (380 B, 20°C) | 1155 (970) | kg/m3 |
| Viscosity (25°C) | 390 | mPa·s |
| Viscosity (380 A, 25°C, 380 B, 25°C) | 1000 (75 ) | mPa·s |
| Pot Life (100g 20°C) | 160 | hour |
| Potlife 100G 20°C (+ 0.5% Acc 254) (+ 2.0% Acc 254) | 105 (56 ) | minutes |
| Tensile Strength | 73 | MPa |
| Elongation at Break | 10 | % |