Nils Malmgren AB NM Laminating 3070
- Chemical Family
- Epoxy & Epoxy Derivatives
NM Laminating 3070 / H2962 is designed to be used when there are high demands of heat-resistance. Laminates with NM Laminating 3070 / H2962 should first gel at +40°C, that will take about 2 hours and then be post-cured at +150°C. Full cure will take place in approx. 4 hours at +150°C.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Tooling & Moldmaking
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- End Uses
- Mold Making
- Polymer Name
- Epoxy Resins & Compounds
- Color
- Transparent
- Markets
- Industrial
- Technology
- Composite Materials
- Normal Packing
- 5.0 kg, 200.0 kg
- 0.5 kg, 180.0 kg
- Chemical Resistance
- Acetone
- Typical Applications
Producing of epoxy laminates with demands of high heat resistance.
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Plastics and Elastomers End Uses
- Mold Making
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Cleaning Solvent | Acetone | — |
| Resin | NM Laminering 3070 | — |
| Hardener | NM Härdare 2962 | — |
| Mixing Ratio (Weight, Volume) | 100 - 27 (100 - 34.34) | — |
| Density | 1107 | kg/m3 |
| Viscosity (25°C) | 2.5 | mPa·s |
| Pot Life (100g 20°C) | 2 | hour |
| Tensile Strength | 55 | MPa |
| E-Modulus | 2.4 | GPa |
| Tg (30 Minutes 150°C) | 110 | °C |
| Tg (4 Hours 150°C) | 150 | °C |