Technicoll® 9117
- Chemical Family
- Polyurethanes (PU)
Technicoll® 9117 is a transparent contact adhesive.
Product families
- Contact Adhesives
Other characteristics
- Brand
- Technicoll
- Product Type
- Contact Adhesive
- Application Area
- Textiles
- Compatible Substrates & Surfaces
Acrylonitrile Butadiene Styrene (ABS), Coated Surfaces, Composites, Elastomers & Rubbers, Leather, Painted Surfaces, Poly(Methyl Methacrylate) (PMMA), Polyamide, Polycarbonate (PC), Polyethylene Terephthalate (PET), Polyurethane, Polyvinyl Chloride (PVC), Styrene-acrylonitrile Resin (SAN), Textiles, Wood
- Base
- Polyurethane
- Markets
- Consumer Goods
- Industrial
- Pot Life
- approx. 12 hours
- Technology
- Ready-to-Use Products
- Labeling Claims
- Plasticizer-free
- Favoured Substrates
ABS, SAN, PVC-u, PA; Elastomers (PUR and nitrile rubber); Derived timber product; PVC-p, faux leather; Leather, textiles; PUR, PUR-foam; Polycarbonate (PC); Painted and coated surfaces; Polyester (PET); PMMA; Fiber reinforced plastics (FRP); Cellulose ester; Not suitable for: PE, PP, PTFE (Teflon®), POM, silicone, EPDM, EPS, XPS (e.g. Styropor®), metals; Due to the large variety of possible materials and differences in adhesion behavior hazard tests are mandatory before introducing the adhesive into the actual production process.
- Handling Properties
Dilution - Not Necessary, Possible With Technicoll® 8362.; Cleaning - Cured adhesive can only be removed mechanically.
- Field of Application
Technicoll® 9117 is suitable for contact bonding of many different plastics and other materials, especially for plasticised materials. technicoll® 9117 can either be used with or without adding cross linking agent technicoll® 9966. When used in combination with technicoll® 9966, the resistance to plasticisers, aging, water and heat is increased.
- Maximum Time Of Storage
At least 2 years when stored in sealed original packaging in cool and dry places.
- Behaviour At Low Temperature
Not susceptible to frost. Densification at low temperature. Once adjusted to processing temperature: fully employable.
- Preferred Storage Temperature
- 10°C - 25°C
Technical data
Table 1 of 2
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Viscosity (20°C) | approx. 3000 | mPas |
| Density | approx. 0.9 | g/cm³ |
| Processing Temperature | 15 - 25 | °C |
Table 2 of 2
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Hardener / Cross Linking Agent | Technicoll® 9966 | — |
| Mixing Ratio | 100:5 - 100:10 | wt/wt |
| Drying Time (Cold Bonding) | approx. 5 - 10 | minutes |
| Drying Time (Heat Bonding) | min. 30 | minutes |
| Contact Life (Cold Bonding) | approx. 15 | minutes |
| Way Of Application | Two-sided | — |
| Consumption (Two-sided Application) | 150 - 250 | g/m² |
| Cleaning Agent / Material | Technicoll® 8363 | — |
| Cleaning Agent / Material (Metal Cleaning Spray) | Technicoll® 9901 | — |
| Cleaning Agent / Material (Plastics Cleaning Spray) | Technicoll® 9902 | — |
| Cleaning Agent / Tool (Technicoll® 8362, Spray) | Technicoll® 9901 | — |