NUDEC® PC
NUDEC®PC polycarbonate plastic sheets are outstanding for their impact strength and high temperature resistance. For this reason, they are often used for applications in sectors such as construction (roofing, cladding, antivandal urban furniture), security (shields and protective masks, vehicle armor, lamps protection) or the industrial safety sector (protection for machinery, personal protective equipment).
Properties
- Physical Form
- Sheets
Other characteristics
- Brand
- NUDEC
- Density
- 1200.0 - 1200.0 kg/m³
- Features
Chemical Resistant, Excellent Transparency Properties, Flame Retardant, Good Brightness, Good Impact Strength, Good UV Protection, Heat Resistance, Noise Damping
- Polymer Name
- Polycarbonate (PC)
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Storage
An incorrect storage position can lead to permanent deformation.; The sheets should be stored in closed premises that guarantee normal environmental conditions.; The sheets should be stored one on top of the other on flat horizontal surfaces and fully supported over their total area.; The topmost panel should be covered with a sheet of polyethylene or cardboard etc.; NUDEC®PC sheets must not be stored in direct sunlight or under conditions of high humidity and/or temperature as this can have a negative effect of protective film adhesion.
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength Notched (23ºC) | 55.0 | kJ/m² | ISO 179 |
| Elasticity Modulus in Traction | 97.0 | MPa | ISO 527 |
| Elongation (Breakage) | 150.0 | % | ISO 527 |
| Izod Notched (23 ºC) | 72/118 | J/m | ISO 180 |
| Izod Unnotched (23ºC) | 950.0 | J/m | ISO 180 |
| Resistance to Flexion | 2300.0 | MPa | ISO 178 |
| Rockwell Hardness (M/R Scale) | No breakage | MPa | ASTM D-785 |
| Tensile Strength (Breakage) | 72.0 | MPa | ISO 527 |
| Tensile Strength (Deformation) | 60.0 | MPa | ISO 527 |
Table 2 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.2 | g/cm³ | ISO 1183 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion | 146.0 | 10⁻⁵ / °C | ISO 75-2 |
| Heat Deflection Temperature B (0.45 Mpa) | 6.8 | 10⁵ /mK | ISO 75-2 |
| Heat Deflection Temperature A (1.8 Mpa) | 143.0 | °C | ISO 75-2 |
| Maximum Service Temperature | 120.0 | °C | — |
| VICAT Softening Temperature (10 N) | 151.0 | °C | ISO 306 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Light Transmission | 87-91 | % | ASTM D-1003 |
| Refractive Index | 1586.0 | — | ASTM D-542 |