Silikal® RH 65 resin
- CASE Ingredients Features
- Fast CureLow Viscosity
SILIKAL® RH 65 resin s a solvent free, fast curing MMA resin of very low viscosity. It is used for indoor screeds of 5-20 mm on concrete to equalize an uneven concrete surface. Screeds must be overlaid with a Silikal® coating system according to System A – E. The fast curing time of 1 hour, flexibility and filler rich formulation of 1 : 8 makes the mortar economical and can be applied at temperatures between 0°C and 35°C (refer to table of hardener). Hot water loadings must be limited to 60 °C. Excess temperature up to 80 °C will be accepted for a short moment as long as the temperature of the complete layer does not adopt the higher degree.
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Floor Coatings
- Infrastructure Roads & Paving
- Floor Coatings
- Coatings & Markings
Product Families
- Acrylics
Other characteristics
- Brand
- Silikal
- Features
- Fast Cure, Low Viscosity
- Compatible Substrates & Surfaces
- Concrete
- Markets
- Building & Construction
- Paints & Coatings
- Application
Layer thickness must be adjusted to the eveness of the concrete and to the mechanical loading and is recommended between 5 and 20 mm. Lower thickness must be avoided as the curing process will slow down. A higher thickness of more than 20 mm will cause shrinkage and tension. For a proper application mix hardener fi rst to the resin and add fi nally the fi ller mix. Normally there is no need to use pigments, however it could be an option.
- Technology
- CASE Ingredients
- Labeling Claims
- Solvent-free
- Hardener Dosages
* The quantity of hardening powder is always related to the quantity of resin including Additive I.
- Compatible Substrates and Surfaces
- Concrete
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity (20°C) | max. 50 | mPa.s | DIN 53 015 |
| Flow Time (20°C, 4 mm Cup) | 25 - 30 | sec. | DIN 53 211 |
| Density (D₄²⁰) | 0.97 | g/cm³ | DIN 51 757 |
| Flash Point | 10.0 | °C | DIN 51 755 |
| Pot Life (20°C, 100 g, 3 % pbw. Hardening Powder) | approx. 18 min. | — | — |
| Application Temperature | 0 - 35 | °C | — |
| Density (Hardened state) | 1.12 | g/cm³ | DIN 53 479 |
| Ultimate Elongation (Hardened state) | 75.0 | % | DIN 53 455 |
| Hardness (Hardened state) | 40 - 45 | Shore-D | DIN 53 505 |
| Water Absorption (4 Days, Hardened State, 50·50·4 mm) | 125.0 | mg | DIN 53 495 |
| Modulus of elasticity | 205.0 | N/mm² | DIN 53 457 |
| Compressive Strength | 30.0 | N/mm² | DIN 1164 |