Avery Dennison FM 2333
- Chemical Family
- Polyethylenes, PolyolefinsPolyethylenesPolyolefins
Avery Dennison™ FM 2333 is a 36 mil double coated white polyethylene foam with a modified acrylic adhesive. It bonds well to low surface energy materials and has the ability to fill gaps. It is commonly used in general industrial foam applications.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- EIFS & Insulation
- Consumer Electronics
- Flexography
- Flexible Packaging Adhesives
- Tapes & Labels
Product Families
- Pressure Sensitive Adhesives & Tapes
Other characteristics
- Features
Chemical Resistant, Conformable, Dimensional Stability, Excellent Substrate Adhesion, Good Gap Filling Capabilities, High Temperature Resistance, High Tensile Strength, Outdoor Durability, Tear Resistance; Double coated tape construction.; Modified acrylic adhesive for low surface energy substrates.; Polyethylene foam carrier.; Super calendered kraft release liner; Environmental Resistance; Chemical Resistance
- Product Type
- Double Coated Foam Tape
- Application Area
- White Goods
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Printing & Packaging
- Benefits
Dimensional stability and good die cutting characteristics.; Strong bond to low surface energy materials.; Good heat resistance.; Gap filling properties and good conformability.; High tensile strength and tear resistance with excellent die cutting performance.; Two-year warranty.
- Technology
- Ready-to-Use Products
- Common Applications
- Building and Construction
- General Converting
- White Goods
- Print and Packaging
- Product Construction
Liner: 60# White Kraft Adhesive 1: Acrylic Carrier: Polyethylene Foam Adhesive 2: ULNA Acrylic
- Shelf Life Storage
Two years when stored at 64 - 72ºF (18 - 22ºC) / 30 - 70% relative humidity, out of direct sunlight and in original packaging.
- Backing Material Type
- Foam
- Application Technique
It is essential, as with all pressure-sensitive tapes, that the surface to which the tape is applied be clean, dry, and free of grease or oil.; Bond strength is dependent upon the amount of adhesive-to-surface contact developed.; Note that different pressure, time and temperature on different (film / rigid) surface achieves different performance.
- Ready to Use Product Features
- Chemical Resistant
- Conformable
- Dimensional Stability
- Excellent Substrate Adhesion
- Good Gap Filling Capabilities
- High Temperature Resistance
- High Tensile Strength
- Outdoor Durability
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Application Temperature | min. 10 | ºC | — |
| Loop Tack (180º, 20 in (508 mm) / min at Room Temperature), (Substrate SS - Liner - Initial) | 1585.0 | N/m | ASTM D6195 |
| Peel Adhesion (180º, 12 in (300 mm) / min at Room Temperature), (Substrate PP - Liner - 72 hr dwell) | 969.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (300 mm) / min at Room Temperature), (Substrate PP - Unwind - 72 hr dwell) | 969.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (300 mm) / min at Room Temperature), (Substrate SS - Liner - 72 hr dwell) | 1497.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (300 mm) / min at Room Temperature), (Substrate SS - Unwind - 72 hr dwell) | 1497.0 | N/m | ASTM D3330 |
| Service Temperature | -40 to 105 | ºC | — |
| Static Shear Failure Time (180º, 1" sq (6.5 cm2), 1000 g at Room Temperature), (Substrate SS - Liner - 24 hr dwell) | min. 10000 | Mins | ASTM D3654 |
| Thickness (Adhesive 1 - Liner) | 58.0 | µm | ASTM D3652 |
| Thickness (Adhesive 2 - Unwind) | 58.0 | µm | ASTM D3652 |
| Thickness (Carrier) | 787.0 | µm | ASTM D3652 |
| Thickness (Liner) | 89.0 | µm | ASTM D3652 |