Avery Dennison™ FT 8270 is a 7.0 mil double coated tissue with a high performance low VOC modified acrylic adhesive. It bonds very well to low surface energy materials and features good foam bonding properties and high heat resistance. It is commonly used in automotive applications and where low VOC properties are required.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Chassis & Brake
- Exterior & Body
- Interior
- Seating
- Tires
- Consumer Electronics
Product Families
- Pressure Sensitive Adhesives & Tapes
Other characteristics
- Features
Conformable, Dimensional Stability, Excellent Substrate Adhesion, Flexible, Good Moisture Resistance, Heat Resistance, High Performance, Low Outgassing, Low VOC; Double coated tape construction.; Low outgassing high performance modified acrylic adhesive.; Tissue carrier.; Poly coated kraft release liner.; Environmental Resistance; Chemical Resistance
- Product Type
- Double Sided Tape
- Application Area
- Acoustic Barrier, Seats, White Goods
- Acoustic Barrier
- Seats
- White Goods
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Benefits
Dimensional stability and good die cutting characteristics.; Solvent free adhesive with good foam bonding performance.; Good heat resistance.; Flexibility and conformability along with the ability to tear by hand.; Good moisture stability and lay flat properties.
- Technology
- Ready-to-Use Products
- Labeling Claims
- Low VOC
- Solvent-free
- Common Applications
- Automotive
- General Converting
- White Goods
- Transportation
- Product Construction
Liner: 87# White Poly Coated Kraft Adhesive 1: Low VOC Acrylic Carrier: Tissue Adhesive 2: Low VOC Acrylic
- Shelf Life Storage
Two years when stored at 64 - 72ºF (18 - 22ºC) / 30 - 70% relative humidity, out of direct sunlight and in original packaging.
- Backing Material Type
- Foam
- Application Technique
It is essential, as with all pressure-sensitive tapes, that the surface to which the tape is applied be clean, dry, and free of grease or oil.; Bond strength is dependent upon the amount of adhesive-to-surface contact developed.; Note that different pressure, time and temperature on different (film / rigid) surface achieves different performance.
- Ready to Use Product Features
- Conformable
- Dimensional Stability
- Excellent Substrate Adhesion
- Flexible
- Good Moisture Resistance
- Heat Resistance
- High Performance
- Low Outgassing
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Application Temperature | min. 30 | ºC | — |
| Loop Tack (180º, 20 in (508 mm) / min at Room Temperature), (Substrate SS - Liner - Initial) | 528.0 | N/m | ASTM D6195 |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate ABS - Liner - 72 hr dwell) | 1233.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate ABS - Unwind - 72 hr dwell) | 1233.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate SS - Liner - 72 hr dwell) | 704.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate SS - Unwind - 72 hr dwell) | 881.0 | N/m | ASTM D3330 |
| Service Temperature | -40 to 175 | ºC | — |
| Static Shear Failure Time (180º, 1" sq (6.5 cm2), 1000 g), (Substrate SS - Liner - 24 hr dwell) | min. 10000 | Mins | ASTM D3654 |
| Thickness (Adhesive 1 - Liner) | 61.0 | µm | ASTM D3652 |
| Thickness (Adhesive 2 - Unwind) | 61.0 | µm | ASTM D3652 |
| Thickness (Carrier) | 56.0 | µm | ASTM D3652 |
| Thickness (Liner) | 173.0 | µm | ASTM D3652 |