Fas-Flex™ 8615M (#57709M)
- Chemical Family
- Polyethylenes, PolyolefinsPolyethylenesPolyolefins
Avery Dennison™ Fas-Flex™ 8615M (#57709M) is a 15 mil (0.015") flexographic plate mounting tape designed for printing large text and lines, reverse text and solids.
Product families
Applications
- Flexography
Product Families
- Pressure Sensitive Adhesives & Tapes
Other characteristics
- Brand
- Fas-Flex
- Features
Good Printability; Double coated foam tape.; Hard foam carrier.; Low tack acrylic plate mounting adhesive.; Cleanly removable acrylic cylinder side adhesive.; Polypropylene film finer.
- Product Type
- Double Coated Foam Tape, Mounting Tape
- Double Coated Foam Tape
- Mounting Tape
- Markets
- Printing & Packaging
- Benefits
Can help eliminate dot gain, gear marks and banding.; ldeal for printing large text and lines, reverse text and solids.; Allows plate to be repositioned during the mounting process.; Designed to remove cleanly during demounting. leaving no residue on the plate or cylinder.; Easy liner removal during mounting process.
- Technology
- Ready-to-Use Products
- Common Applications
- Print and Packaging
- Product Construction
- Liner
- Polypropylene Film
- Adhesive 1
- Acrylic
- Carrier
- White Polyethylene Foam
- Adhesive 2
- ULNA Acrylic
- Shelf Life Storage
One year when stored at 64 - 72ºF (18 - 22ºC) / 30 - 70% relative humidity, out of direct sunlight and in original packaging.
- Backing Material Type
- Foam
- Application Technique
It is essential, as with all pressure-sensitive tapes, that the surface to which the tape is applied be clean, dry, and free of grease or oil.; Bond strength is dependent upon the amount of adhesive-to-surface contact developed.; Note that different pressure, time and temperature on different (film / rigid) surface achieves different performance.
- Ready to Use Product Features
- Good Printability
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Application Temperature | min. 18 | ºC | — |
| Dynamic Shear (180º, 2 in (50.8 mm) / min), (Substrate SS - Liner - Initial) | 18209.0 | N/m | ASTM D1002 |
| Intermittent Operating Temperature | max. 95 | ºC | — |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate SS - Liner - 72 hr dwell) | 810.1 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate SS - Liner - Initial) | 722.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate SS - Unwind - 72 hr dwell) | 687.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (305 mm) / min), (Substrate SS - Unwind - Initial) | 652.0 | N/m | ASTM D3330 |
| SAFT Failure Time (1" sq (6.5 cm2), 500 g), (Substrate SS - Liner - Initial) | 350.0 | Mins | ASTM D4498 |
| SAFT Fail Temperature (1" sq (6.5 cm2), 500 g), (Substrate SS - Liner - Initial) | 205.0 | ºC | — |
| Static Shear Failure Time (180º, 1" sq (6.5 cm2), 1000 g at Room Temperature), (Substrate SS - Liner - Initial) | min. 10000 | Mins | ASTM D3654 |
| Thickness (Adhesive 1 - Liner) | 51.0 | µm | ASTM D3652 |
| Thickness (Adhesive 2 - Unwind) | 51.0 | µm | ASTM D3652 |