Avery Dennison FBR 8950 12 PT
- Chemical Family
- Polyethylene Terephthalate (PET)
Avery Dennison™ FBR 8950 12 PT is a 4.0 mil double coated polyester with a general purpose rubber adhesive and a heavy board release liner. It bonds well to polyurethane foams, fabrics and low surface energy materials. It is commonly used for foam bonding and general purpose attachment in automotive and appliance applications.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Chassis & Brake
- Exterior & Body
- Interior
- Seating
- Tires
- Consumer Electronics
Product Families
- Pressure Sensitive Adhesives & Tapes
Other characteristics
- Features
Excellent Stiffness, General Purpose, High Tensile Strength; Double coated tape construction.; General purpose rubber adhesive.; Polyester film carrier.; 12 point poly coated kraft board release liner.
- Product Type
- Double Sided Tape
- Application Area
- Acoustic Barrier, Seats, White Goods
- Acoustic Barrier
- Seats
- White Goods
- Compatible Substrates & Surfaces
- Fibers & Fabrics
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Benefits
Dimensional stability and good die cutting characteristics.; Strong bond to a wide variety of materials and good foam bonding performance.; High tensile strength and good converting performance; Heavyweight and stiffness allow for easy handling.; Two-year warranty.
- Technology
- Ready-to-Use Products
- Common Applications
- Automotive
- General Converting
- White Goods
- Transportation
- Product Construction
Liner: Natural 12 Pt Board Adhesive 1: Rubber Carrier: Polyester Adhesive 2: ULNA Rubber
- Shelf Life Storage
Two years when stored at 64 - 72ºF (18 - 22ºC) / 30 - 70% relative humidity, out of direct sunlight and in original packaging.
- Backing Material Type
- Polyester
- Application Technique
It is essential, as with all pressure-sensitive tapes, that the surface to which the tape is applied be clean, dry, and free of grease or oil.; Bond strength is dependent upon the amount of adhesive-to-surface contact developed.; Note that different pressure, time and temperature on different (film / rigid) surface achieves different performance.
- Ready to Use Product Features
- Excellent Stiffness
- General Purpose
- High Tensile Strength
- Compatible Substrates and Surfaces
- Fibers & Fabrics
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Application Temperature | min. 10 | ºC | — |
| Loop Tack (180º, 20 in (508 mm) / min at Room Temperature), (Substrate SS - Liner - Initial) | 1761.0 | N/m | ASTM D6195 |
| Peel Adhesion (180º, 12 in (300 mm) / min at Room Temperature), (Substrate PP - Liner - 72 hr dwell) | 1233.0 | N/m | ASTM D3330 |
| Peel Adhesion (180º, 12 in (300 mm) / min at Room Temperature), (Substrate SS - Liner - 72 hr dwell) | 1409.0 | N/m | ASTM D3330 |
| Service Temperature | -40 to 70 | ºC | — |
| Static Shear Failure Time (180º, 1" sq (6.5 cm2), 1000 g at Room Temperature), (Substrate SS - Liner - 24 hr dwell) | min. 10000 | Mins | ASTM D3654 |
| Thickness (Adhesive 1 - Liner) | 36.0 | µm | ASTM D3652 |
| Thickness (Adhesive 2 - Unwind) | 53.0 | µm | ASTM D3652 |
| Thickness (Carrier) | 13.0 | µm | ASTM D3652 |
| Thickness (Liner) | 328.0 | µm | ASTM D3652 |
| Thickness (Total Caliper) | 429.0 | µm | ASTM D3652 |
| Thickness (Total Caliper without Liner) | 102.0 | µm | ASTM D3652 |