Dioki GPPS® 607X

Chemical Family: Styrenics

Dioki GPPS® 607X is transparent general purpose polystyrene exhibiting good melt flow properties. Dioki GPPS® 607X is basically intended for extrusion and foam extrusion products. This polystyrene grade is characterized by good thermal and dimensional stability of molded products Dioki GPPS® 607X does not contain any lubricant.

Properties

Physical Form: Solid

Product families

Applications

Consumer Goods — Other Consumer Goods Applications

Building & Construction — Building Materials

Wall Panels

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: Dioki GPPS
Polymer Name: General Purpose Polystyrene (GPPS)
Melt Flow Index: 6.6 - 6.6 g/10 min
Processing Methods: Extrusion, Foam Extrusion
Markets: Building & Construction
Consumer Goods
PACKAGING: DİOKİ GPPS 603® is packed in polyethylene bags of 25 kg on wooden pallets having dimensions of 110x130 cm as 1 pallet net 1.375 kg. (Depend on the costumers demand, net 1.250 kg bigbag can be supplied) The pallets are covered and secured with stretch film.
Application: Production of foamed extruded polystyrene panels (XPS), in various foam applications.
Technology: Plastics
Packaging Type: Bags
Material Features: Dimensional Stability
Ease of Handling
Excellent Transparency Properties
General Purpose
Good Mechanical Properties
Good Thermal Stability
High Melt Flow
Storage and Handling: DİOKİ GPPS 603® should be protected from direct sunlight and rain/water. If possible, it should stored in dry, cool and closed area.
Plastics and Elastomers End Uses: General Purpose
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion
Foam Extrusion

Technical data

Table 1 of 4

6 rows

Characteristic	Value	Unit	Method
Elongation at Break	1,3	%	ASTM D 638
Izod Impact Resistance, Notched (23°C)	12,0	J/m	ASTM D 256
Modulus	3180	MPa	ASTM D 790
Strength	80	MPa	ASTM D 790
Strength at Break	42	MPa	ASTM D 638
Tensile Modulus	3200	MPa	ASTM D 638

Table 2 of 4

2 rows

Characteristic	Value	Unit	Method
Heat Distortion Temp. (Metot B, 0.45 MPa)	92	°C	ASTM D 648
Vicat Softening Temperature (Rate B, 10N)	106	°C	ASTM D 1525