Dioki HIPS® 803
- Chemical Family
- High-Impact Polystyrene (HIPS)Styrenics
Dioki HIPS® 803 is high impact polystyrene has high impact strength and temperature resistance and specially developed for processing by extrusion and thermoforming.
Properties
- Physical Form
- Solid
Product families
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
- Consumer Electronics
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
- Styrenics
Other characteristics
- Brand
- Dioki HIPS
- Polymer Name
- High Impact Polystyrene (HIPS)
- Melt Flow Index
- 3.6 - 3.6 g/10 min
- Processing Methods
- Extrusion, Thermoforming
- Markets
- Consumer Goods
- Electrical & Electronics
- Printing & Packaging
- PACKAGING
DİOKİ GPPS 603® is packed in polyethylene bags of 25 kg on wooden pallets having dimensions of 110x130 cm as 1 pallet net 1.375 kg. (Depend on the costumers demand, net 1.250 kg bigbag can be supplied) The pallets are covered and secured with stretch film.
- Application
Extruded and thermoformed products, mainly cups used for diary products, other thermoformed plastic containers used in food processing industry, mixing with DİOKİ GPPS®/HIPS® grades, injection molded products having small dimensions and thick walls, but it does not use with ABS and SAN plastomers.
- Technology
- Plastics
- Packaging Type
- Bags
- Material Features
- High Impact Performance
- Thermal Shock Resistant
- Storage and Handling
DİOKİ GPPS 603® should be protected from direct sunlight and rain/water. If possible, it should stored in dry, cool and closed area.
- Plastics and Elastomers End Uses
- Appliances
- Consumer Applications
- Containers
- Cups
- Food Containers
- Food Packaging
- Front Spoiler
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Thermoforming
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break | 66 | % | D 638 |
| Izod Impact Resistance, Notched (23°C) | 94 | J/m | D 256 |
| Modulus | 1780 | MPa | D 790 |
| Strength | 38 | MPa | D 790 |
| Strength at Break | 23 | MPa | D 638 |
| Strength at Yield | 20 | MPa | D 638 |
| Tensile Modulus | 1800 | MPa | D 638 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temp. (Metot B, 0.45 MPa) | 84 | °C | D 648 |
| Vicat Softening Temperature (Rate B, 10N) | 100 | °C | D 1525 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index (200°C/ 5kg) | 3,6 | g/10 min | D 1238 |
Table 4 of 4
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Shrinkage | 0,4-0,6 | % |
| Processed in Melt Temperature Range | 160-230 | °C |
| Tool Temperature | 20-60 | °C |