Dioki GPPS® 603

Chemical Family: Styrenics

Dioki GPPS® 603 Dioki Petrokimya GPPS® 603 is transparent general purpose polystyrene exhibiting good melt flow properties. Dioki GPPS® 603 is basically intended for extrusion, foam extrusion and injection molding of thick-walled molded products. This polystyrene grade is characterized by good thermal and dimensional stability of molded products.

Properties

Physical Form: Solid

Product families

Applications

Consumer Goods — Other Consumer Goods Applications

Building & Construction — Building Materials

Wall Panels

Healthcare & Pharma — Medical

Other Medical Applications

Printing & Packaging — Packaging

Healthcare Packaging
Non-Food Consumer Packaging

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: Dioki GPPS
Polymer Name: General Purpose Polystyrene (GPPS)
Melt Flow Index: 3.0 - 3.0 g/10 min
Processing Methods: Extrusion, Foam Extrusion, Injection Molding
Markets: Building & Construction
Consumer Goods
Healthcare & Pharma
Printing & Packaging
PACKAGING: DİOKİ GPPS 603® is packed in polyethylene bags of 25 kg on wooden pallets having dimensions of 110x130 cm as 1 pallet net 1.375 kg. (Depend on the costumers demand, net 1.250 kg bigbag can be supplied) The pallets are covered and secured with stretch film.
Application: Production of foamed extruded polystyrene panels (XPS), in various foam applications, packaging in cosmetics, shower cabin and medicine, mixing with other DİOKİ GPPS®/HIPS® grades.
Technology: Plastics
Packaging Type: Bags
Material Features: Dimensional Stability
Ease of Handling
Excellent Transparency Properties
General Purpose
Good Mechanical Properties
Good Thermal Stability
High Melt Flow
Storage and Handling: DİOKİ GPPS 603® should be protected from direct sunlight and rain/water. If possible, it should stored in dry, cool and closed area.
Plastics and Elastomers End Uses: Cosmetic Packaging
General Purpose
Medical/Healthcare Applications
Pharmaceutical Packaging
Toys
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion
Foam Extrusion
Injection Molding

Technical data

Table 1 of 4

6 rows

Characteristic	Value	Unit	Method
Elongation at Break	1,6	%	ASTM D 638
Izod Impact Resistance, Notched (23°C)	12	J/m	ASTM D 256
Modulus	3225	MPa	ASTM D 790
Strength	92	MPa	ASTM D 790
Strength at Break	44	MPa	ASTM D 638
Tensile Modulus	3200	MPa	ASTM D 638

Table 2 of 4

2 rows

Characteristic	Value	Unit	Method
Heat Distortion Temp. (Metot B, 0.45 MPa)	93	°C	ASTM D 648
Vicat Softening Temperature (Rate B, 10N)	107	°C	ASTM D 1525

Table 3 of 4