Dioki HIPS® 703
- Chemical Family
- High-Impact Polystyrene (HIPS)Styrenics
Dioki HIPS® 703 is high impact polystyrene specially developed for processing by extrusion and thermoforming. Dioki HIPS® 703 has excellent resistance to hydrocarbons used in the fridge sector as blowing agent for PU insulating foams. This polystyrene grade is characterized by high impact strength and good tensile strength.
Properties
- Physical Form
- Solid
Product families
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
- Consumer Electronics
Product Families
- Styrenics
Other characteristics
- Brand
- Dioki HIPS
- Polymer Name
- High Impact Polystyrene (HIPS)
- Melt Flow Index
- 3.5 - 3.5 g/10 min
- Processing Methods
- Extrusion, Thermoforming
- Markets
- Consumer Goods
- Electrical & Electronics
- PACKAGING
DİOKİ GPPS 603® is packed in polyethylene bags of 25 kg on wooden pallets having dimensions of 110x130 cm as 1 pallet net 1.375 kg. (Depend on the costumers demand, net 1.250 kg bigbag can be supplied) The pallets are covered and secured with stretch film.
- Application
Extruded and thermoformed for; interior refrigerator walls, food processing industry and other extruded products. It is miscible with other DİOKİ GPPS®/HIPS® Polystyrene grades, but it is not miscible with ABS and SAN plastomers.
- Technology
- Plastics
- Packaging Type
- Bags
- Material Features
- Excellent Tensile Properties
- High Impact Performance
- Hydrocarbon Resistant
- Storage and Handling
DİOKİ GPPS 603® should be protected from direct sunlight and rain/water. If possible, it should stored in dry, cool and closed area.
- Plastics and Elastomers End Uses
- Appliances
- Consumer Applications
- Cups
- Household Goods
- Thermoforming Applications
- Toys
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Thermoforming
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break | 55 | % | D 638 |
| Izod Impact Resistance, Notched (23°C) | 96 | J/m | D 256 |
| Modulus | 1460 | MPa | D 790 |
| Strength | 32 | MPa | D 790 |
| Strength at Break | 18 | MPa | D 638 |
| Strength at Yield | 13 | MPa | D 638 |
| Tensile Modulus | 1390 | MPa | D 638 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temp. (Metot B, 0.45 MPa) | 81 | °C | D 648 |
| Vicat Softening Temperature (Rate B, 10N) | 101 | °C | D 1525 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index (200°C/ 5kg) | 3,5 | g/10 min | D 1238 |
Table 4 of 4
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Shrinkage | 0,4-0,6 | % |
| Processed in Melt Temperature Range | 160-230 | °C |
| Tool Temperature | 20-60 | °C |