Dioki HIPS® 810
- Chemical Family
- High-Impact Polystyrene (HIPS)Styrenics
Dioki HIPS® 810 is high impact polystyrene specially developed for injection molding. Dioki HIPS® 810 exhibits high melt flow properties, mold cavities fully filled up.
Properties
- Physical Form
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Dioki HIPS
- Polymer Name
- High Impact Polystyrene (HIPS)
- Melt Flow Index
- 10.0 - 10.0 g/10 min
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- PACKAGING
DİOKİ GPPS 603® is packed in polyethylene bags of 25 kg on wooden pallets having dimensions of 110x130 cm as 1 pallet net 1.375 kg. (Depend on the costumers demand, net 1.250 kg bigbag can be supplied) The pallets are covered and secured with stretch film.
- Application
Injection molding of thin-walled molded products, injection molded technical components of high impact strength and bending properties.
- Technology
- Plastics
- Packaging Type
- Bags
- Material Features
- High Impact Performance
- Storage and Handling
DİOKİ GPPS 603® should be protected from direct sunlight and rain/water. If possible, it should stored in dry, cool and closed area.
- Plastics and Elastomers End Uses
- Appliances
- Consumer Applications
- Food Containers
- Food Packaging
- Toys
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break | 67 | % | D 638 |
| Izod Impact Resistance, Notched (23°C) | 87 | J/m | D 256 |
| Modulus | 2000 | MPa | D 790 |
| Strength | 36 | MPa | D 790 |
| Strength at Break | 17 | MPa | D 638 |
| Strength at Yield | 19 | MPa | D 638 |
| Tensile Modulus | 2000 | MPa | D 638 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temp. (Metot B, 0.45 MPa) | 80,5 | °C | D 648 |
| Vicat Softening Temperature (Rate B, 10N) | 97 | °C | D 1525 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index (200°C/ 5kg) | 10,0 | g/10 min | D 1238 |
Table 4 of 4
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Shrinkage | 0,4-0,6 | % |
| Processed in Melt Temperature Range | 160-230 | °C |
| Tool Temperature | 20-60 | °C |