ALCOM® LD PC 1000 18002 CC1001-18

Chemical Family: Polycarbonate (PC)

MOCOM Compounds Alcom® LD PC 1000 18002 CC1001-18 is a polycarbonate base polymer with a special filler/additive system that provides translucency, high light transmission, light scattering, and good flow. It is approved by GS93016 and is suitable for applications in lighting and light transparent components, such as lamp covers, display elements, and operating elements. For processing, injection molding should be used with a melt temperature of 270-300°C and a mold temperature of 80-100°C. The product must be pre-dried at 120°C in a dry air (dessiccant) dryer for 2-3 hours with a maximum moisture content of less than 0.02%.

Product families

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays
Lighting

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: ALCOM
Polymer Name: Polycarbonate (PC)
Fillers Included: Proprietary
Flexural Modulus: 2450.0 - 2450.0 MPa
Processing Methods: Injection Molding
Markets: Consumer Goods
Electrical & Electronics
Technology: Plastics
OEM Standards: BMW
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Good Flow
Good Light Diffusion
High Light Transmission
Light Scattering
Translucent
OEM Specifications: BMW GS 93016
Storage Condition: Store in dry, protected from light.
Pre-Drying Conditions: 120 °C in a dry air (dessiccant) dryer for 2-3 h
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Displays
Lamp Covers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 8

10 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2450.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	76.0	MPa	ISO 178
Tensile Modulus	2400.0	MPa	ISO 527
Tensile Stress at Yield	62.0	MPa	ISO 527
Tensile Elongation at Yield	6.0	%	ISO 527
Tensile Elongation at Break	90.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	no break	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	no break	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	10.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	10.0	kJ/m²	ISO 179/1eA

Table 2 of 8

1 row

Characteristic	Value	Unit	Method
Density	1190.0	kg/m³	ISO 1183

Table 3 of 8

2 rows

Characteristic	Value	Unit	Method
Vicat B50	142.0	°C	ISO 306
HDT / A (1.8 MPa)	128.0	°C	ISO 75-1/-2

Table 4 of 8

1 row

Characteristic	Value	Unit
Moisture Content	max. 0.02	%

Table 5 of 8

12 rows

Characteristic	Value	Unit	Method
Total Transmission T(Y) (d=1,0mm, A, 2°)	90.0	%	ISO 13468
Total Transmission T(Y) (d=2,0mm, A, 2°)	89.0	%	ISO 13468
Total Transmission T(Y) (d=3,0mm, A, 2°)	89.0	%	ISO 13468
Total Transmission T(Y) (d=4,0mm, A, 2°)	89.0	%	ISO 13468
Haze T(Y) (d=1.0 mm, A, 2°)	42.0	%	ISO 13468
Haze T(Y) (d=2.0 mm, A, 2°)	62.0	%	ISO 13468
Haze T(Y) (d=3.0 mm, A, 2°)	74.0	%	ISO 13468
Haze T(Y) (d=4.0 mm, A, 2°)	81.0	%	ISO 13468
Half Power Angle T(Y) (d=1mm, A, 2°)	2.0	Degree	—
Half Power Angle T(Y) (d=2mm, A, 2°)	2.0	Degree	—
Half Power Angle T(Y) (d=3mm, A, 2°)	3.0	Degree	—
Half Power Angle T(Y) (d=4mm, A, 2°)	3.0	Degree	—

Table 6 of 8

5 rows

Characteristic	Value	Unit	Method
Flammability (0.75 m)	V - 2	class	UL 94
Flammability (1.5 mm)	HB	class	UL 94
UL Recognition	yes	—	—
Glow Wire (GWFI, 850°C, 1mm)	Passed	—	DIN EN 60695
Glow Wire (GWFI, 850°C, 2mm)	Passed	—	DIN EN 60695

Table 7 of 8