ALCOM® PA66 910/1 NU SV1057-03MCF

Chemical Family: Polyamides

MOCOM Compounds ALCOM® PA66 910/1 NU SV1057-03MCF is a Polyamide 66 base polymer with a metallic effect and low tendency to flow lines, fast solidifying, and easy release (demolding). It is used in the automotive, electrical and electronic, and building and construction markets for injection molded parts and housings. The pre-drying conditions for this material are 80°C in a dry air (dessiccant) dryer for 2-12 h depending on moisture content. The processing injection molding parameters are melt temperature 270-290°C and mold temperature 40-80°C.

Product families

Applications

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: ALCOM
Polymer Name: Polyamide 66 (PA 66)
Flexural Modulus: 3600.0 - 3600.0 MPa
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Fast Solidifying
Good Mold Release
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: 80 °C in a dry air (dessiccant) dryer for 2-12 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Automotive Applications
Construction Applications
Electrical/Electronic Applications
Housings
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

8 rows

Characteristic	Value	Unit	Method
Flexural Modulus	3600.0	MPa	ISO 178
Flexural Strength	120.0	MPa	ISO 178
Tensile Modulus	3900.0	MPa	ISO 527
Tensile Stress at Yield	90.0	MPa	ISO 527
Tensile Elongation at Yield	4.0	%	ISO 527
Tensile Elongation at Break	7.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	28.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	3.0	kJ/m²	ISO 179/1eA

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1180.0	kg/m³	ISO 1183

Table 3 of 6

3 rows

Characteristic	Value	Unit	Method
Vicat B50	240.0	°C	ISO 306
HDT / A (1.8 MPa)	85.0	°C	ISO 75-1/-2
DSC (Melt Point)	260.0	°C	ISO 11357

Table 4 of 6