TEDUR® L 9113-2
- Chemical Family
- Polyphenylene Sulfide (PPS)
MOCOM Compounds TEDUR® L 9113-2 is a Polyphenylene Sulfide injection molding grade with a filler/additive system of 60% glass fibers. It has a high stiffness and is suitable for use in the Automotive and Machinery markets. Pre-drying conditions should be in a dry air (dessiccant) dryer at 130-140°C for 2-4 hours, depending on moisture content. Processing Injection molding should be done with a melt temperature of 320-340°C and a mold temperature greater than 140°C. It is recommended to protect from light and store at a temperature not exceeding 30°C.
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- TEDUR
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 22600.0 - 22600.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- High Stiffness
- High Temperature Resistance
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 130-140 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 22600.0 | MPa | ISO 178 |
| Flexural Strength | 230.0 | MPa | ISO 178 |
| Tensile Modulus | 23000.0 | MPa | ISO 527 |
| Flexural Deflection (Maximum Force) | 1.1 | % | ISO 178 |
| Tensile Strength at Break | 140.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 0.8 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 24.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1870.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 279.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 280.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | 1 x 10¹² | Ohm | DIN EN 62631-3-2 |
Table 5 of 6
1 row| Characteristic | Value | Method |
|---|---|---|
| Glow Wire (GWFI, 960°C, 2mm) | Passed | DIN EN 60695 |
Table 6 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | min. 140 | °C |
| Melt Temperature | 320 - 340 | °C |