ALTECH® PSU FC 1000/100
- Chemical Family
- Polysulfones
MOCOM Compounds ALTECH® PSU FC 1000/100 is a polysulfone base polymer with good flow, used for injection molding of machinery, electrical and electronic parts, and food contact parts. Pre-drying conditions should be done in a dry air (dessiccant) dryer at 130-150°C for 3-4 hours, or an air circulating dryer at 130-150°C for 3-4 hours. Processing injection molding should be done with a melt temperature of 330-380°C and a mold temperature of 120-140°C.
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polysulfone (PSU)
- Flexural Modulus
- 2800.0 - 2800.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- Food Contact Acceptable
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Food Contact Acceptable
- Good Flow
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 130-150 °C for 3-4 h; In an air circulatIng dryer 130-150 °C for 3-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2800.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 93.0 | MPa | ISO 178 |
| Tensile Modulus | 2600.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 78.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 5.6 | % | ISO 527 |
| Tensile Elongation at Break | 65.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 5.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1230.0 | kg/m³ | ISO 1183 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 173.0 | °C | ISO 75-1/-2 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 120 - 140 | °C |
| Melt Temperature | 330 - 380 | °C |
Table 5 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (24h) | 0.6 - 0.9 | % | ISO 294-4 |