ALCOM® AWL 109/10 WT1218-11LB
MOCOM Compounds ALCOM® AWL 109/10 WT1218-11LB is a base polymer - acrylonitrile/butadiene/styrene/copolymer modified with polycarbonate, containing a filler/additive system of 10% special filler and special features of being highly reflective, opaque, and highly heat-stabilized. It is suitable for use in the automotive and various market segments, primarily for use in lighting and light-blocking components such as light guides and reflectors.
Product families
Applications
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
- Blends & Alloys
Other characteristics
- Brand
- ALCOM
- Density
- 1180.0 - 1180.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Fillers Included
- Mineral
- Proprietary
- Additives Included
- Heat Stabilizer
- Material Features
- Excellent Opacity
- Good Light Reflection
- Heat Stabilized
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-90 °C for 2-4 h; In an air circulatIng dryer 80-90 °C for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 75.0 | MPa | ISO 178 |
| Tensile Modulus | 2500.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 50.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 3.0 | % | ISO 527 |
| Tensile Elongation at Break | 13.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 100.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 93.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 20.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 115.0 | MPa | ISO 2039-1 |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1180.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 109.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 100.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 85.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.2 | % | ISO 13468 |
Table 6 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
| Flammability (3.0 mm) | HB | class | UL 94 |
| Fire Behavior FMVSS (2.0 mm) | Passed | — | FMVSS 302/DIN 75200 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 230 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 17.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |
| Shrinkage (24h) | 0.6 - 0.8 | % | ISO 294-4 |