ALTECH® PP-H A 2030/250 GF30 CP
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H A 2030/250 GF30 CP is a polypropylene homopolymer with a 30% glass fiber filler/additive system that is heat-stabilized, impact-modified, easy to release (demolding), processing-stabilized, and chemically coupled. This product is suitable for automotive, building, and construction market segments and is used for injection molded parts, interior decoration/finishing, clothing/fasteners, and exterior parts. Typical applications include functional components, housings, and seals. It offers high strength, stiffness, and excellent surface finish.
Product families
Applications
- Exterior & Body
- Interior
- Textile Manufacturing
- Housings & Enclosures
Product Families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Fillers Included
- Glass Fiber
- Additives Included
Heat Stabilizer, Impact Modifier, Processing Stabilizer; Heat Stabilizer; Impact Modifier; Processing Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Chemically Coupled
- Good Mold Release
- Heat Aging Resistant
- Heat Stabilized
- Impact Modified
- Processing Stability
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Construction Applications
- Fasteners
- Housings
- Seals
- Textile Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 5500.0 | MPa | ISO 178 |
| Flexural Strength | 120.0 | MPa | ISO 178 |
| Tensile Modulus | 6000.0 | MPa | ISO 527 |
| Tensile Strength at Break | 80.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 4.1 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 57.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 14.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1110.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 134.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 144.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 163.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 1.5 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.3 - 0.5 | % | ISO 294-4 |