WIC PA6 20 BK
- Chemical Family
- Polyamides
WIC PA6 20 BK is a polyamide 6 base polymer filled with 20% carbon fiber and colored black. It has medium viscosity and heat aging stabilization. For processing, it requires injection molding at a melt temperature of 250-270°C and a mold temperature of 60-100°C. The increased thermal conductivity must be taken into account under certain conditions. This product is suitable for the automotive and sport market segment.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- WIC
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Medium Viscosity
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in a dry-air dryer for 2-8h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 13100.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 280.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 15500.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 8200.0 | MPa | ISO 527 |
| Tensile Strength (Dry) | 190.0 | MPa | ISO 527 |
| Tensile Strength (Conditioned) | 106.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Dry) | 1.8 | % | ISO 527 |
| Tensile Strength at Break (Dry) | 170.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 1.9 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 4.8 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 58.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 70.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1230.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 5.72 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 207.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357-1/-3 |
| DSC (Melt Point, Dry) | min. 220 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance (Conditioned) | max. 100 | Ohm | IEC 62631-3-2 |
| Specific Volume Resistance (Dry) | 100.0 | Ohm*m | IEC 62631-3-1 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR, Dry) | 50.0 | cm³/10min | ISO 1133 |
| MVR Temperature (Dry) | 300.0 | °C | — |
| MVR Load (Dry) | 1.2 | kg | — |
| Molding Shrinkage (parallel, Dry) | 0.2 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal, Dry) | 0.5 | % | ISO 294-4, 2577 |