AMODEL® A-1230 L BK324
- Chemical Family
- Polyamides
MOCOM Compounds AMODEL® A-1230 L BK324 is a polyphthalamide material with 30% talcum filler/additive system, suitable for injection molding with a melt temperature of 320-345°C and a mold temperature of 80-140°C. It has special features such as low warpage and a slip agent, and is used in the automotive and machinery markets for functional components, housings, and other injection molded parts.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- AMODEL
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Talc
- Flexural Modulus
- 6000.0 - 6000.0 MPa
- Additives Included
- Slip Agent
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Low Warpage
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 110-120 °C for 3-6 h; Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Housings
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6000.0 | MPa | ISO 178 |
| Flexural Strength | 178.0 | MPa | ISO 178 |
| Tensile Modulus | 6000.0 | MPa | ISO 527 |
| Tensile Strength at Break | 110.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.3 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 3.5 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1430.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 138.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 315.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.05 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 320 - 345 | °C |
| Mould Temperature | 80 - 140 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.1 - 1.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.1 - 1.5 | % | ISO 294-4 |