CELLIDOR® CP FC 400.01-08

Chemical Family: Cellulose & Cellulosics

MOCOM Compounds CELLIDOR® CP FC 400.01-08 is a base polymer composed of cellulose acetate propionate containing 8% phthalate-free plasticiser. It is suitable for injection molding parts, food contact and typical applications such as toothbrushes. Pre-drying conditions should be in an air circulating dryer at 60-90°C for 2-4 h, depending on moisture content, with a maximum moisture content of 0.15%. Processing should be injection molding with a melt temperature of 180-230°C and a mold temperature of 40-80°C. To ensure quality, keep it dry and protected from light.

Product families

Plastics — Basic Thermoplastics

Cellulosics

Other characteristics

Brand: CELLIDOR
Density: 1200.0 - 1200.0 kg/m³
End Uses: Toothbrushes
Polymer Name: Cellulose Acetate Propionate (CAP)
Additives Included: Plasticizer (Phthalate-free)
Markets: Consumer Goods
Applications: Consumer Goods — Housewares
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Bio-based
Conflict minerals-free
Food Contact Acceptable
PAH-free
PFOA-free
PFOS-free
Material Features: Food Contact Acceptable
Heat Aging Resistant
Non Phthalate Plasticizer
Storage Condition: Store in dry, protected from light.
Pre-Drying Conditions: In an air circulatIng dryer 60-90 °C for 2-4 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Toothbrushes
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

11 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2000.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	52.0	MPa	ISO 178
Tensile Modulus	1900.0	MPa	ISO 527
Tensile Stress at Yield	47.0	MPa	ISO 527
Tensile Elongation at Yield	4.5	%	ISO 527
Tensile Elongation at Break	12.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	185.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	165.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	15.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	5.5	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H132/30)	95.0	MPa	ISO 2039-1

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1200.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Vicat B50	100.0	°C	ISO 306
HDT / A (1.8 MPa)	100.0	°C	ISO 75-1/-2

Table 4 of 6