CELLIDOR® B 500-15

Chemical Family: Cellulose & Cellulosics

MOCOM Compounds CELLIDOR® B 500-15 is a cellulose acetate butyrate base polymer with 15% phthalate-free plasticiser. It is suitable for injection molding with melt temperatures ranging from 180-230°C and mold temperatures from 40-80°C. It has the special features of low odor and is used for various applications.

Product families

Plastics — Basic Thermoplastics

Cellulosics

Other characteristics

Brand: CELLIDOR
Density: 1170.0 - 1170.0 kg/m³
Polymer Name: Cellulose Acetate Butyrate (CAB)
Additives Included: Plasticizer (Phthalate-free)
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Bio-based
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Low Odor
Non Phthalate Plasticizer
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In an air circulatIng dryer 50-80 °C for 2-4 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

9 rows

Characteristic	Value	Unit	Method
Flexural Modulus	1100.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	30.0	MPa	ISO 178
Tensile Modulus	1200.0	MPa	ISO 527
Tensile Stress at Yield	27.0	MPa	ISO 527
Tensile Elongation at Yield	3.6	%	ISO 527
Tensile Elongation at Break	30.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	no break	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	25.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H132/30)	45.0	MPa	ISO 2039-1

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1170.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Vicat B50	74.0	°C	ISO 306
HDT / A (1.8 MPa)	69.0	°C	ISO 75-1/-2

Table 4 of 6