CELLIDOR® CP 300-10

Chemical Family: Cellulose & Cellulosics

MOCOM Compounds CELLIDOR® CP 300-10 is a base polymer composed of cellulose acetate propionate, with a 10% phthalate-free plasticiser. It is suitable for use in the production of toothbrushes and other products. It should be pre-dried in an air circulating dryer at temperatures between 60-90°C for 2-4 hours, depending on the moisture content. For injection molding, the melt temperature should be between 180-230°C and the mold temperature should be between 40-80°C. No extra sentence required.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Housewares

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Product Families

Plastics — Basic Thermoplastics

Cellulosics

Other characteristics

Brand: CELLIDOR
Density: 1200.0 - 1200.0 kg/m³
End Uses: Hearing Aid, Toothbrushes
Polymer Name: Cellulose Acetate Propionate (CAP)
Additives Included: Plasticizer (Phthalate-free)
Markets: Consumer Goods
Electrical & Electronics
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Bio-based
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Non Phthalate Plasticizer
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In an air circulatIng dryer 60-90 °C for 2-4 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Hearing Aid
Toothbrushes
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

9 rows

Characteristic	Value	Unit	Method
Flexural Modulus	1900.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	50.0	MPa	ISO 178
Tensile Modulus	1950.0	MPa	ISO 527
Tensile Stress at Yield	45.0	MPa	ISO 527
Tensile Elongation at Yield	4.1	%	ISO 527
Tensile Elongation at Break	15.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	190.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	20.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H358/30)	65.0	MPa	ISO 2039-1

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1200.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Vicat B50	96.0	°C	ISO 306
HDT / A (1.8 MPa)	92.0	°C	ISO 75-1/-2

Table 4 of 6