CELLIDOR® B 501-10

Chemical Family: Cellulose & Cellulosics

MOCOM Compounds CELLIDOR® B 501-10 is a Base Polymer of Cellulose Acetate Butyrate that has been pre-dried in either a dry air (dessiccant) dryer at 50-70°C for 1-2 h or an air circulating dryer at 50-70°C for 2-4 h. It is suitable for Processing Injection molding with a melt temperature of 190-235°C and a mold temperature of 40-80°C and is formulated with a phthalate-free plasticiser and other additives to provide good chemical resistance, high light transmission, high surface quality, processing stabilization, injection molding grade, good haptics, and good weathering resistance, making it suitable for various market segments and applications areas with typical applications.

Product families

Plastics — Basic Thermoplastics

Cellulosics

Other characteristics

Brand: CELLIDOR
Density: 1170.0 - 1170.0 kg/m³
Polymer Name: Cellulose Acetate Butyrate (CAB)
Additives Included: Plasticizer (Phthalate-free), Processing Stabilizer; Plasticizer (Phthalate-free); Processing Stabilizer
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Bio-based
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Chemical Resistant
Good Haptics
Good Weather Stability
High Light Transmission
Non Phthalate Plasticizer
Processing Stability
Superior Surface Quality
UV Resistant
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In an air circulatIng dryer 50-70 °C for 2-4 h; In a dry air (dessiccant) dryer 50-70 °C for 1-2 h
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

11 rows

Characteristic	Value	Unit	Method
Flexural Modulus	1650.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	42.0	MPa	ISO 178
Tensile Modulus	1600.0	MPa	ISO 527
Tensile Stress at Yield	38.0	MPa	ISO 527
Tensile Elongation at Yield	4.0	%	ISO 527
Tensile Elongation at Break	13.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	no break	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	no break	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	24.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	4.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H132/30)	65.0	MPa	ISO 2039-1

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density	1170.0	kg/m³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Vicat B50	85.0	°C	ISO 306
HDT / A (1.8 MPa)	85.0	°C	ISO 75-1/-2

Table 4 of 5