CELLIDOR® CP 2825-11

Chemical Family: Cellulose & Cellulosics

MOCOM Compounds CELLIDOR® CP 2825-11 is a base polymer of cellulose acetate propionate with a phthalate-free filler/additive system of plasticiser and light stabilizer. It has special features of easy flow, high toughness, high stiffness, and UV stabilization, making it suitable for various market segments and applications areas, such as sports equipment and spectacle lenses. For injection molding, the melt temperature should be set between 190-235°C and the mold temperature should be between 40-80°C.

Product families

Plastics — Basic Thermoplastics

Cellulosics

Other characteristics

Brand: CELLIDOR
Density: 1200.0 - 1200.0 kg/m³
End Uses: Spectacle Lenses, Sporting Goods
Polymer Name: Cellulose Acetate Propionate (CAP)
Additives Included: Light Stabilizer, Plasticizer (Phthalate-free), UV Stabilizer; Light Stabilizer; Plasticizer (Phthalate-free); UV Stabilizer
Markets: Consumer Goods
Applications: Consumer Goods — Sports & Recreation
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Bio-based
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Excellent Toughness
Good Flow
High Stiffness
Light Stabilized
Non Phthalate Plasticizer
UV Resistant
UV Stabilized
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In a dry air (dessiccant) dryer 50-70 °C for 1-2 h; Dependant on moisture content; In an air circulatIng dryer 50-70 °C for 2-4 h
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Spectacle Lenses
Sporting Goods
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

11 rows

Characteristic	Value	Unit	Method
Flexural Modulus	1900.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	50.0	MPa	ISO 178
Tensile Modulus	1800.0	MPa	ISO 527
Tensile Stress at Yield	40.0	MPa	ISO 527
Tensile Elongation at Yield	4.0	%	ISO 527
Tensile Elongation at Break	14.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	225.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	170.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	20.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	6.5	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H132/30)	67.0	MPa	ISO 2039-1

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density	1200.0	kg/m³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Vicat B50	95.0	°C	ISO 306
HDT / A (1.8 MPa)	100.0	°C	ISO 75-1/-2

Table 4 of 5