ALPERFORM® PA IM NC2595-14
MOCOM Compounds ALPERFORM® PA IM NC2595-14 is a high-impact, modified and heat-stabilized polyamide 66 base polymer, suitable for application in cable ties. For optimal performance, it should be pre-dried in a dry air (dessiccant) dryer at temperatures below 80°C for 2-12 hours, depending on the moisture content, with a maximum moisture content of 0.15%. The injection molding temperature should be between 270-290°C, and the mold temperature should be between 40-80°C.
Properties
- Physical Form
- Masterbatch
- Solid
Product families
- Additive Masterbatches
- Antioxidants & Stabilizers
- Performance Additives
- Processing Aids
Other characteristics
- Brand
- ALPERFORM
- Carrier
- Polybutylene Terephthalate (PBT), Resin-based
- Polybutylene Terephthalate (PBT)
- Resin-based
- Functions
- Heat Stabilizer, Impact Modifier, Stabilizer
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Cable Ties
- Plastics and Elastomers Functions
- Heat Stabilizer
- Impact Modifier
- Stabilizer
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2000.0 | MPa | ISO 178 |
| Flexural Strength | 80.0 | MPa | ISO 178 |
| Tensile Modulus | 2100.0 | MPa | ISO 527 |
| Tensile Strength | 53.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 35.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 65.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 10.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1090.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 59.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 260.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1 - 1.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.3 - 1.7 | % | ISO 294-4 |