ALCOM® PP 620/1 WT1433-05LB
MOCOM Compounds ALCOM® PP 620/1 WT1433-05LB is a polypropylene homopolymer with 8% special filler, 30% mineral, and highly reflective, opaque features. It is used in the automotive and lighting market segments for light guides, reflectors, and light blocking components. The processing for injection molding is done at a melt temperature of 230-270°C and a mold temperature of 20-90°C.
Product families
Applications
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
- Polyolefins
Other characteristics
- Brand
- ALCOM
- Features
Excellent Opacity, Good Light Reflection, High Reflectivity, Light Blocking
- Functions
- Resin
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Mineral, Proprietary
- Mineral
- Proprietary
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Material Features
- Excellent Opacity
- Good Light Reflection
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-100 °C for 2-3 h; In an air circulatIng dryer 80-100 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- LED Housing
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 4500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 54.0 | MPa | ISO 178 |
| Tensile Modulus | 3900.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 31.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 2.8 | % | ISO 527 |
| Tensile Elongation at Break | 5.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 23.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 12.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 1.5 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1220.0 | kg/m³ | ISO 1183 |
Table 3 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 100.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 86.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 166.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 87.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.3 | % | ISO 13468 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 90 | °C |
| Melt Temperature | 230 - 270 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 25.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.9 - 1.1 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 0.9 | % | ISO 294-4 |