WIC PP 40 BK
- Chemical Family
- PolyolefinsPolypropylenes (PP)
WIC PP 40 BK is a black material with heat-age stabilization properties intended for use in automotive and sports applications. The base polymer is polypropylene, and it contains 40% carbon fiber as a filler. Prior to processing via injection molding, the material must be pre-dried at 80°C for 2-4 hours, depending on its moisture content, which should not exceed 0.10%. During injection molding, the material should be melted at temperatures ranging from 210 to 260°C, with a mold temperature between 30 and 60°C.
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- WIC
- Polymer Name
- Polypropylene Copolymer
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in an air circulating dryer for 2-4h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 17800.0 | MPa | ISO 178 |
| Flexural Strength | 153.0 | MPa | ISO 178 |
| Tensile Modulus | 15500.0 | MPa | ISO 527 |
| Tensile Strength | 93.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 36.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 9.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1130.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 1.17 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 156.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 160.0 | °C | ISO 11357-1/-3 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.1 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | max. 10 | Ohm | IEC 62631-3-2 |
| Specific Volume Resistance | 0.1 | Ohm*m | IEC 62631-3-1 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 210 - 260 | °C |
| Mould Temperature | 30 - 60 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 2.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Molding Shrinkage (parallel) | 0.1 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal) | 0.1 | % | ISO 294-4, 2577 |