WIC PP 30 BK IM1
- Chemical Family
- PolyolefinsPolypropylenes (PP)
WIC PP 30 BK IM1 is a black polypropylene compound with 30% carbon fiber filler. It is suitable for injection molding and must be dried at 80°C for 2-4 hours prior to processing to achieve a moisture content of 0.10% maximum. The recommended melt temperature range is between 210 and 260°C, with a mold temperature of 30 to 60°C. The material has been formulated with heat stabilization and impact modification, making it a suitable choice for use in automotive and sports applications. It is also resistant to wear and tear and has a good surface finish.
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- WIC
- Polymer Name
- Polypropylene Copolymer
- Fillers Included
- Carbon Fiber
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Impact Modified
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in an air circulating dryer for 2-4h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9300.0 | MPa | ISO 527 |
| Tensile Strength | 60.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 5.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 70.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 23.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1050.0 | kg/m³ | ISO 1183 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| DSC (Melt Point) | 160.0 | °C | ISO 11357-1/-3 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.1 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 210 - 260 | °C |
| Mould Temperature | 30 - 60 | °C |
Table 6 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 5.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 5.0 | kg | — |