WIC PP 30 BK LE2
- Chemical Family
- PolyolefinsPolypropylenes (PP)
WIC PP 30 BK LE2 is a black polypropylene composite with 30% carbon fiber filler, designed for injection molding in the automotive and sports industries. Prior to processing, it is recommended to pre-dry the material at 80°C for 2-4 hours, depending on the moisture content—which should be no higher than 0.10%. The injection molding process requires a melt temperature of 210-260°C and a mold temperature of 30-60°C, taking into account the material's increased thermal conductivity under certain conditions. This composite also features low emission, heat age stabilization, and UV stabilization.
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- WIC
- Polymer Name
- Polypropylene Copolymer
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Low Emissions
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in an air circulating dryer for 2-4h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 13500.0 | MPa | ISO 527 |
| Tensile Strength | 90.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 1.5 | % | ISO 527 |
| Tensile Strength at Break | 87.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.3 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 43.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 33.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1090.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 1.5 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 149.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | min. 160 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.1 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 210 - 260 | °C |
| Mould Temperature | 30 - 60 | °C |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 12.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Molding Shrinkage (parallel) | 0.2 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal) | 0.4 | % | ISO 294-4, 2577 |