WIC PA66+6I/6T 20 BK
- Chemical Family
- Polyamides
WIC PA66+6I/6T 20 BK is a carbon fiber reinforced polyamide 66 thermoplastic that is black in color and heat aging stabilized. It is suitable for automotive and sporting applications. Pre-drying Conditions include drying in a dry-air dryer at 80°C for 2-8 hours, depending on the moisture content, with a maximum moisture content of 0.12%. Processing Conditions include injection molding at a melt temperature of 280-300°C and mold temperature of 80-120°C. The increased thermal conductivity of this material must be taken into account when using it.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- WIC
- Polymer Name
- PA 66+PA 6I/6T
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in a dry-air dryer for 2-8h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 12000.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 11700.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 270.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 240.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 14700.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 13300.0 | MPa | ISO 527 |
| Tensile Strength (Dry) | 182.0 | MPa | ISO 527 |
| Tensile Strength (Conditioned) | 149.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 1.8 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 2.4 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 30.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 34.0 | kJ/m² | ISO 179/1eU |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1230.0 | kg/m³ | ISO 1183 |
Table 3 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 5 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR, Dry) | 30.0 | cm³/10min | ISO 1133 |
| MVR Temperature (Dry) | 300.0 | °C | — |
| MVR Load (Dry) | 1.2 | kg | — |