WIC PP 10 BK LE
- Chemical Family
- PolyolefinsPolypropylenes (PP)
WIC PP 10 BK LE is a polypropylene-based filler with 10% carbon fiber and black color, designed for injection molding with a melt temperature of 210-260°C and a mold temperature of 30-60°C. It offers low emission, heat aging stabilization, and is suitable for use in the Automotive and Sport market segments. Under certain conditions, increased thermal conductivity should also be considered.
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- WIC
- Polymer Name
- Polypropylene Copolymer
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Low Emissions
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in an air circulating dryer for 2-4h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 4500.0 | MPa | ISO 178 |
| Flexural Strength | 94.0 | MPa | ISO 178 |
| Tensile Modulus | 6000.0 | MPa | ISO 527 |
| Tensile Strength | 60.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 4.5 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 32.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 25.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 970.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 1.74 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 102.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 147.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 160.0 | °C | ISO 11357-1/-3 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.1 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | max. 1500 | Ohm | IEC 62631-3-2 |
| Specific Volume Resistance | 10.0 | Ohm*m | IEC 62631-3-1 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 210 - 260 | °C |
| Mould Temperature | 30 - 60 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 33.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Molding Shrinkage (parallel) | 0.5 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal) | 0.4 | % | ISO 294-4, 2577 |