WIC PA66 30 BK
- Chemical Family
- Polyamides
WIC PA66 30 BK is a Polyamide 66 base polymer filled with 30% carbon fiber and black in color. It has medium viscosity and heat aging stabilized features, making it suitable for use in the Automotive and Sport Market Segments. Processing Conditions involve injection molding, with a melt temperature of 280-300°C and mold temperature of 80-120°C. It is important to note that the increased thermal conductivity must be taken into account when processing the material.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- WIC
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Medium Viscosity
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in a dry-air dryer for 2-8h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 18500.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 12000.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 260.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 220.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 22500.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 14000.0 | MPa | ISO 527 |
| Tensile Strength (Dry) | 210.0 | MPa | ISO 527 |
| Tensile Strength (Conditioned) | 152.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 1.5 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 2.8 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 55.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 60.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1270.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 5.06 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 (Dry) | 248.0 | °C | ISO 306 |
| HDT / A (Dry, 1.8 MPa) | 256.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 260.0 | °C | ISO 11357-1/-3 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance (Conditioned) | max. 10 | Ohm | IEC 62631-3-2 |
| Specific Volume Resistance (Dry) | 0.1 | Ohm*m | IEC 62631-3-1 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR, Dry) | 12.0 | cm³/10min | ISO 1133 |
| MVR Temperature (Dry) | 300.0 | °C | — |
| MVR Load (Dry) | 1.2 | kg | — |
| Molding Shrinkage (parallel, Dry) | 0.1 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal, Dry) | 0.5 | % | ISO 294-4, 2577 |