WIC PA66 10 BK
- Chemical Family
- Polyamides
WIC PA66 10 BK is a polyamide 66 base polymer filled with 10% carbon fiber and is black in color. It has medium viscosity and is heat-age stabilized, making it suitable for the automotive and sports market segments. For injection molding, the melt temperature should be between 280-300°C and the mold temperature should be between 80-120°C. Additionally, when using this polymer, the increased thermal conductivity must be taken into consideration. To ensure optimal performance, the polymer should be stored dry and protected from light.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- WIC
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Medium Viscosity
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in an air circulating dryer for 2-8h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9000.0 | MPa | ISO 527 |
| Tensile Strength | 145.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.5 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 30.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 3.5 | kJ/m² | ISO 179/1eA |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1180.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 6.04 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 247.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 260.0 | °C | ISO 11357-1/-3 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | max. 2350 | Ohm | IEC 62631-3-2 |
| Specific Volume Resistance | 26.0 | Ohm*m | IEC 62631-3-1 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 40.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Molding Shrinkage (parallel) | 0.2 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal) | 0.9 | % | ISO 294-4, 2577 |