ALTECH® ECO PA6 4230/100 GF10 MR20
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® ECO PA6 4230/100 GF10 MR20 is a heat-stabilized polyamide 6 blend with 10% glass fibers and 20% mineral. Pre-drying is recommended at 80°C in a dry air (dessiccant) dryer for 2-12 hours, depending on moisture content, with a maximum moisture content of 0.15%. It is suitable for injection molding with a melt temperature of 270-290°C and a mold temperature of 80-100°C. It is typically used in the automotive market for engine covers and housings, and should be stored in a dry and light-protected environment not exceeding 30°C to ensure optimal properties.
Product families
Applications
- Powertrain & UTH
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH® ECO
- Features
Good Flow, Heat Stabilized, Low Warpage, Superior Surface Quality
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Flexural Modulus
- 5900.0 - 5900.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Recycled
- Material Features
- Good Flow
- Heat Stabilized
- Low Warpage
- Superior Surface Quality
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Engine Covers
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 5900.0 | MPa | ISO 178 |
| Flexural Strength | 160.0 | MPa | ISO 178 |
| Tensile Modulus | 6700.0 | MPa | ISO 527 |
| Tensile Strength at Break | 90.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 4.5 | kJ/m² | ISO 179/1eA |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1360.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 0.31 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 190.0 | °C | ISO 75-1/-2 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |