ALTECH® ECO PA6 2030/219 GF30 IM
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® ECO PA6 2030/219 GF30 IM is a heat-stabilized, impact-modified, injection molding grade containing 30% glass fibers and recycled material. It should be pre-dried at 80°C in a dry air (dessiccant) dryer for 2-12 hours depending on moisture content. During processing, the melt temperature should be set between 270-290°C and the mold temperature between 80-100°C. Typical applications include housings.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALTECH® ECO
- End Uses
- Housings
- Features
- Heat Stabilized, Impact Modified
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer, Impact Modifier
- Heat Stabilizer
- Impact Modifier
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Recycled
- Material Features
- Heat Stabilized
- Impact Modified
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 8000.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 5000.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 185.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 115.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 9000.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 5000.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 125.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.0 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 67.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 4.8 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 54.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1320.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 0.58 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 205.0 | °C | ISO 75-1/-2 |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 1.5 mm) | HB | class | UL 94 |
| UL Recognition (Dry) | yes | — | — |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.5 - 0.7 | % | ISO 294-4 |