ALTECH® ECO PA6 3230/100 GB20 GF10
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® ECO PA6 3230/100 GB20 GF10 is a polyamide 6 base polymer with a filler/additive system consisting of 20% glass beads and 10% glass fibers, which provides low warpage, heat stabilization, and fast solidifying properties. It is recommended to pre-dry the material at 80°C in a dry air (dessiccant) dryer for 2-12 hours, depending on moisture content, with a maximum moisture content of 0.15%. For processing injection molding, the melt temperature should be between 270-290°C and the mold temperature should be between 80-100°C. Typical applications for this material include various industrial components.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH® ECO
- Features
- Fast Solidifying, Heat Stabilized, Low Warpage
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Bead, Glass Fiber
- Glass Bead
- Glass Fiber
- Flexural Modulus
- 5400.0 - 5400.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Recycled
- Material Features
- Fast Solidifying
- Heat Stabilized
- Low Warpage
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 5400.0 | MPa | ISO 178 |
| Flexural Strength | 150.0 | MPa | ISO 178 |
| Tensile Modulus | 5800.0 | MPa | ISO 527 |
| Tensile Strength at Break | 95.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.2 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1350.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 2.89 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 190.0 | °C | ISO 75-1/-2 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.5 - 0.7 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |